LNP™ LUBRILOY™ R2000A compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRILOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RQOn5O_LNPLUBRILOYR2000Acompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRILOY* R2000A is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRILOY* Compound RL Product reorder name: R2000A |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 2.6 | % | ASTM D955 |
| Transverse flow : 24 hours | 2.6 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 2.6 | % | ISO 294-4 |
| Flow direction : 24 hours | 2.6 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.30 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.43 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2000 | MPa | ASTM D638 |
| -- | 2100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 47.8 | MPa | ASTM D638 |
| Yield | 43.8 | MPa | ISO 527-2 |
| Fracture | 43.4 | MPa | ASTM D638 |
| Fracture | 43.5 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 6.0 | % | ASTM D638 |
| Yield | 8.8 | % | ISO 527-2 |
| Fracture | 39 | % | ASTM D638 |
| Fracture | 30 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 1930 | MPa | ASTM D790 |
| -- | 2200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 67.8 | MPa | ASTM D790 |
| -- | 69.9 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.32 | ASTM D3702 Modified | |
| With Self-Static | 0.27 | ASTM D3702 Modified | |
| Wear Factor - Washer | 12.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 75 | J/m | ASTM D256 |
| 23°C 2 | 6.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | No Break | ASTM D4812 | |
| 23°C 3 | 140 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 6.40 | J | ASTM D3763 |
| -- | 1.70 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 66.1 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 62.8 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 67.0 | °C | ISO 75-2/Af |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 271 - 282 | °C | |
| Mold Temperature | 82.2 - 93.3 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® 1022H | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| SOLLAMID A 2700 - A 2730 FV 40 | Krisoll Resinas Plásticas Ltda. | Nylon 66 | SOLLAMID |
| APEX® 84132 | Teknor Apex Company | PVC, Flexible | APEX® |
| Elvax庐 3135SB | DuPont Packaging & Industrial Polymers | EVA | Elvax® |
| LEXAN™ HPX4REU resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |