LNP™ LUBRICOMP™ RFL33 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RQ35W3_LNPLUBRICOMPRFL33compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RFL33 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Also known as: LNP* LUBRICOMP* Compound RFL-4033 Product reorder name: RFL33 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.30 - 0.50 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5900 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 126 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.5 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 4800 | MPa | ISO 178 |
| Flexural Stress | 176 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 3(23°C) | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 35 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, unannealed, 64.0mm span | 261 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 243 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 3.9E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 9.5E-5 | cm/cm/°C | ISO 11359-2 |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® HDM 504 | Marco Polo International, Inc. | HDPE | MARPOL® |
| ResMart Ultra PC LF | ResMart | PC | ResMart Ultra |
| Celanex® 3309HRT | Celanese Corporation | PBT | Celanex® |
| CYCOLOY™ CM6140 resin | SABIC Innovative Plastics | PC+ABS | CYCOLOY™ |
| Gallonprene® GP420-4501 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |