Amilan® CM3001G-15
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Toray Resin Company |
| Trademark: | Amilan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RPxPfG_Amilan-CM3001G-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Amilan® CM3001G-15 is a Polyamide 66 (Nylon 66) product filled with 15% glass fiber. It is available in Asia Pacific, Europe, or North America. Typical application: Automotive. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Part Marking Code |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.26 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | |||
| Across Flow : 3.00 mm 1 | 1.0 to 1.4 | -- | % | |
| Flow : 3.00 mm 2 | 0.70 to 1.0 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 1.0 | -- | % | |
| Saturation, 23°C | 7.2 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | |||
| M-Scale, 23°C | 95 | -- | ||
| R-Scale, 23°C | 120 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress | ISO 527-2 | |||
| -40°C | 155 | 145 | MPa | |
| 23°C | 110 | 90.0 | MPa | |
| 80°C | 65.0 | 50.0 | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Break, -40°C | 2.0 | -- | % | |
| Break, 23°C | 2.0 | 4.5 | % | |
| Break, 80°C | 7.5 | -- | % | |
| Flexural Modulus | ISO 178 | |||
| -40°C | 6600 | 6300 | MPa | |
| 23°C | 5800 | 3700 | MPa | |
| 80°C | 2800 | 2200 | MPa | |
| Flexural Stress | ISO 178 | |||
| -40°C | 225 | 190 | MPa | |
| 23°C | 180 | 135 | MPa | |
| 80°C | 115 | 85.0 | MPa | |
| Shear Strength (23°C) | 80.0 | -- | MPa | ASTM D732 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 30 | -- | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature | 265 | -- | °C | DSC |
| CLTE - Flow | 4.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 2000 | -- | J/kg/°C | |
| Thermal Conductivity | 0.36 | -- | W/m/K |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+12 to 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 20 | -- | kV/mm | IEC 60243-1 |
| Dielectric Constant 3 | IEC 60250 | |||
| 23°C, 50 Hz | 4.30 | -- | ||
| 23°C, 1 kHz | 4.10 | -- | ||
| 23°C, 1 MHz | 3.60 | -- | ||
| Dissipation Factor 4 | IEC 60250 | |||
| 23°C, 50 Hz | 0.040 | -- | ||
| 23°C, 1 kHz | 0.040 | -- | ||
| 23°C, 1 MHz | 0.040 | -- |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.794 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80x80x3 |
| 2 . | 80x80x3mm |
| 3 . | 60% RH |
| 4 . | 60% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 D TFE 18 SI 2 | RTP Company | Nylon 612 | RTP |
| Ultramid® B3ZG7 OSI BK23273 | BASF Corporation | Nylon 6 | Ultramid® |
| Adell PP RA-18 | Adell Plastics, Inc. | PP Copolymer | Adell PP |
| ExxonMobil™ PP7032E2 | ExxonMobil Chemical | PP Impact Copolymer | ExxonMobil™ |
| POLYfill PPH GF5020 PD1 VT2 | Polykemi AB | PP Homopolymer | POLYfill |