LNP™ FARADEX™ DS0036I compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ FARADEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ROX5nc_LNP-FARADEX-DS0036I-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP FARADEX DS0036I is a compound based on Polycarbonate resin containing 15% Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding, High Impact, Non-Brominated & Non-Chlorinated Flame Retardant. Also known as: LNP* FARADEX* Compound DS-1003 FR HI Product reorder name: DS0036I |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.29 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 24 hr | 0.50 | % | |
| Flow : 24 hr | 0.40 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 57.0 | MPa | |
| Break | 55.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 3.8 | % | |
| Break | 4.0 to 8.0 | % | |
| Flexural Modulus | 2600 | MPa | ISO 178 |
| Flexural Stress | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 120 | J/m | ASTM D256 |
| 23°C 1 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1800 | J/m | ASTM D4812 |
| 23°C 2 | 85 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 136 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 125 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : -40 to 40°C | 6.7E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 5.6E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+3 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+4 | ohms·cm | ASTM D257 |
| Shielding Effectiveness (3.00 mm) | 40 to 55 | dB | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (2.10 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 93.3 to 121 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TORZEN® GT3300HSL BK20 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| Niblan F20 AE/V0 | Soredi S.p.a. | PBT | Niblan |
| Badamid® UL A703 GF30 FR HF | Bada AG | Nylon 66 | Badamid® |
| KOCETAL® WH702 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Karina SILVER PVC COMPOUND -E 808-47/ 14-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |