HANWHA CLNB-8141S
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Hanwha Chemical |
| Trademark: | HANWHA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RO7Pya_HANWHA-CLNB-8141S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HANWHA Wire & Cable Compound CLNB-8141S is a low density, crosslinkable polyethylene compound designed for medium voltage(66kV and higher) power cable insulation requiring a high degree of cleanness. It has a extremely low level of contamination and proper balance of non-staining antioxidant and peroxide to ensure thermal stability and optimum cure levels. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Degree of Crosslinking | 82 | % | ASTM D2765A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset | 75 | % | IEC 60811-2-1 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 1 sec) | 50 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 19.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 550 | % | ASTM D638 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (136°C, 168 hr) | < -10 | % | ASTM D573 |
| Change in Ultimate Elongation in Air (136°C, 168 hr) | < -10 | % | ASTM D573 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | > 22 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 2.28 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 4.0E-4 | ASTM D150 |
| Additional Information |
|---|
| Failures after 21 days:0 in 10% Igepal C 0 -6300 in 100% Igepal C 0 -630 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 115 - 130 | °C |
| Extrusion instructions |
|---|
| Cure Temperature : 320~390°CLine Speed : 3~8 m/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 A TFE 15 | RTP Company | Nylon 6 | RTP |
| NYCOA Polyamide 6215 HS | Nycoa (Nylon Corporation of America) | Nylon 612 | NYCOA Polyamide |
| China PPS Staple Fiber | Sichuan Deyang Chemical Co., Ltd | PPS | China PPS |
| Karina GRAY PVC COMPOUND 550-18/363-A | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lupol® GP3202 | LG Chem Ltd. | PP, Unspecified | Lupol® |