Order Products : sales@su-jiao.com
CERTENE™ LDF-120J
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RNTIqu_CERTENE-LDF-120J.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LDF-120J is a certified prime resin, designed for production of general purpose, blown films. LDF-120J features an excellent combination of easy processability, good melt strength and good impact strength. LDF-120J applications include agricultural film, freezer film, liners, shrink film and a blend component for improved melt strength. LDF-120J contains no slip and high antiblock. LDF-120J complies with FDA regulation 21CFR 177.1520(c)3.1a and with most international regulations concerning the use of Polyethylene in contact with food articles. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 38 µm, blown film | 197 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm, blown film | 254 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm, blown film | 10.7 | MPa | ASTM D882 |
| TD : Yield, 38 µm, blown film | 10.3 | MPa | ASTM D882 |
| MD : Broken, 38 µm, blown film | 29.0 | MPa | ASTM D882 |
| TD : Broken, 38 µm, blown film | 24.1 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 150 | % | ASTM D882 |
| TD : Broken, 38 µm, blown film | 550 | % | ASTM D882 |
| Dart Drop Impact 1(38 µm, Blown Film) | 140 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, blown film | 300 | g | ASTM D1922 |
| TD : 38 µm, blown film | 70 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.1 µm, Blown Film) | 50 | ASTM D2457 | |
| Haze (38.1 µm, Blown Film) | 11 | % | ASTM D1003 |
| Additional Information |
|---|
| Film Specimen:1.5 mils (38 µm) film; melt temperature 390°F; blow-up-ratio 2.5 :1. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 199 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Riteflex® XFR 655 | Celanese Corporation | TPC-ET | Riteflex® |
| XYRON™ L654V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| Hybrid B2026G30 | Ravago Manufacturing Americas, LLC | PC+PBT | Hybrid |
| KumhoSunny PBT 3730FG | Shanghai KumhoSunny Plastics Co., Ltd. | PBT | KumhoSunny PBT |
| LNP™ STAT-KON™ ZX05043 compound | SABIC Innovative Plastics Europe | PPE+PS | LNP™ STAT-KON™ |