Sumikon® PM-6530
| Category: | Phenolic , Phenolic |
| Manufacturer: | SBHPP |
| Trademark: | Sumikon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RN6ceF_SumikonPM6530.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SUMIKON® PM-6530 (Type Black) is Glass fiber and Inorganic filler filled resol resin (non-anmonia phenolic) molding compound with good mechanical property and good electronic property. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.84 | g/cm³ | JIS K6911 |
| Molding Shrinkage - Flow | 0.13 | % | JIS K6911 |
| Water Absorption (Equilibrium) | 0.10 | % | JIS K6911 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 96.0 | MPa | JIS K6911 |
| Flexural Modulus | 13400 | MPa | JIS K6911 |
| Flexural Strength | 130 | MPa | JIS K6911 |
| Compressive Strength | 220 | MPa | JIS K6911 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.7 | kJ/m² | JIS K6911 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 300 | °C | JIS K6911 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | 10 | kV/mm | JIS K6911 |
| Arc Resistance | 179 | sec | JIS K6911 |
| Insulation Resistance | JIS K6911 | ||
| -- 2 | 7.0E+12 | ohms | JIS K6911 |
| -- 3 | 1.0E+12 | ohms | JIS K6911 |
| Note Message | |
|---|---|
| 1 . | Method B (step by step) |
| 2 . | As molded |
| 3 . | After boiling |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ J-700GP | Prime Polymer Co., Ltd. | PP Homopolymer | Prime Polypro™ |
| Trithene® TS 7035 | Petroquimica Triunfo | LDPE | Trithene® |
| DIALAC® S710A | UMG ABS, Ltd. | ASA | DIALAC® |
| Ecoflex® Supersoft 00-30 | Smooth-On, Inc | Silicone | Ecoflex® Supersoft |
| Hylar® 5000 | Solvay Specialty Polymers | PVDF | Hylar® |