Sarlink® TPE EE-1195B BLK X (PRELIMINARY DATA)
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RMhXWg_Sarlink-TPE-EE-1195B-BLK-X-PRELIMINARY-DATA-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sarlink EE-1100 Series are general purpose extrusion grades exhibiting good elastic performance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shaw D, 1 sec | 43 | ISO 868 | |
| Shaw D, 5 seconds | 39 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| Transverse flow : 100% strain | 6.80 | MPa | ISO 37 |
| Flow : 100% strain | 5.50 | MPa | ISO 37 |
| Tensile Strength | ISO 37 | ||
| Transverse flow : Fracture | 13.5 | MPa | ISO 37 |
| Flow : Fracture | 12.4 | MPa | ISO 37 |
| Tensile Elongation | ISO 37 | ||
| Transverse flow : Fracture | 660 | % | ISO 37 |
| Flow : Fracture | 580 | % | ISO 37 |
| Tear Strength | ISO 34-1 | ||
| Transverse flow | 60 | kN/m | ISO 34-1 |
| Flow | 52 | kN/m | ISO 34-1 |
| Compression Set (70°C, 22 hr) | 62 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air - Across Flow (110°C, 1008 hr) | -26 | % | ISO 188 |
| Changes in tensile stress upon fracture in air- Transverse flow (110°C, 1008 hr) | -17 | % | ISO 188 |
| Change in Shore Hardness in Air (support a, 110 c, 1008 hr) | 3.8 | ISO 188 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Apparent Shear Viscosity - @ 206 1/sec (200°C) | 240 | Pa·s |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 170 - 190 | °C | |
| Middle Temperature | 175 - 195 | °C | |
| Front Temperature | 180 - 205 | °C | |
| Nozzle Temperature | 180 - 205 | °C | |
| Processing (Melt) Temp | 180 - 205 | °C | |
| Mold Temperature | 15.0 - 40.0 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 176°F (80°C). |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® CLEAR G 830 Rnew | Arkema | Nylon Copolymer | Rilsan® |
| UBESTA 3020X15 | UBE America, Inc. | Nylon 12 | UBESTA |
| CALP WW175 | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| Hanwha Total PE R901U | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | LLDPE | Hanwha Total PE |
| Jam HD-60507/UV | Jam Petrochemical Company | HDPE | Jam |