Versaflex™ HC MT226 Datasheet,TPE,PolyOne Corporation-SHANGHAI SUSHENG

Message
Versaflex™HC MT226 is a transparent high-performance TPE material, converted to medical catheter research and development. VersaflexTM HC MT226 adopts a special formula and does not use any plasticizer. New Products. Commercial norms have not yet been established. • Flexible • Special formula without plasticizer • High transparency

General Information
Features	Good flexibility Definition, high
Uses	Pipe fittings Medical/nursing supplies
Agency Ratings	FDA not rated ISO 10993 Part 4 ISO 10993 Part 5 USP Class VI
RoHS Compliance	RoHS compliance
Appearance	Clear/transparent
Forms	Particle
Processing Method	Extrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.888	g/cm³	ASTM D792

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A, 10 sec)	84		ASTM D2240

Films	Nominal Value	Unit	Test Method
Oxygen Permeability (21°C, 1800 µm)	390	cm³·mm/m²/atm/24 hr	ASTM D3985
Oxygen Transmission Rate (21°C, 1800 µm)	210	cm³/m²/24 hr	ASTM D3985

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress (300% Strain, 23°C)	6.10	MPa	ASTM D412
Tensile Strength (Break, 23°C)	11.0	MPa	ASTM D412
Tensile Elongation (Break, 23°C)	600	%	ASTM D412
Compression Set			ASTM D395B
22°C, 22 hr	20	%	ASTM D395B
45°C, 22 hr	51	%	ASTM D395B
70°C, 22 hr	67	%	ASTM D395B

Fill Analysis	Nominal Value	Unit	Test Method
Apparent Viscosity			ASTM D3835
200°C, 1340 sec^-1	172	Pa·s	ASTM D3835
200°C, 11200 sec^-1	36.0	Pa·s	ASTM D3835

Extrusion	Nominal Value	Unit
Melt Temperature	182 - 204	°C
Die Temperature	171 - 199	°C

Extrusion instructions
Color concentrates with polypropylene (PP), ethylene vinyl acetate (EVA), or low density polyethylene (PE) carriers are most suitable for coloring Versaflex™ HC MT226. Improved color dispersion can be achieved by using higher melt flow concentrates (with a melt flow from 25 - 40g/10 min). Typical loadings for color concentrates are 1% to 5% by weight. Liquid color can be used, but mineral oil based carriers may have a significant effect on the final hardness value. Concentrates based on PVC should not be used. A high color match consistency can be obtained by using precolored compounds available from GLS. The final determination of color concentrate suitability should be determined by customer trials.Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP).Drying is not RequiredRear: 330F-370FCenter: 350F-400FFront: 360F-420FScrew: 100-500RPM

Extrusion instructions

Color concentrates with polypropylene (PP), ethylene vinyl acetate (EVA), or low density polyethylene (PE) carriers are most suitable for coloring Versaflex™ HC MT226. Improved color dispersion can be achieved by using higher melt flow concentrates (with a melt flow from 25 - 40g/10 min). Typical loadings for color concentrates are 1% to 5% by weight. Liquid color can be used, but mineral oil based carriers may have a significant effect on the final hardness value. Concentrates based on PVC should not be used. A high color match consistency can be obtained by using precolored compounds available from GLS. The final determination of color concentrate suitability should be determined by customer trials.Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP).Drying is not RequiredRear: 330F-370FCenter: 350F-400FFront: 360F-420FScrew: 100-500RPM

Category:	TPE , Thermoplastic Elastomer
Manufacturer:	PolyOne Corporation
Trademark:	Versaflex™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	RMes2Q_Versaflex-HC-MT226.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP ESD C 205 UV	RTP Company	Nylon 66	RTP
RTP 799 A X 128004 D	RTP Company	LDPE	RTP
Leona™ 1402S	Asahi Kasei Chemicals Corporation	Nylon 66	Leona™
LUVOCOM® 1-8864/ES	LEHVOSS Group	Nylon 66	LUVOCOM®
POCAN® S 7926 000000	LANXESS GmbH	PBT	POCAN®