AFFINITY™ PL 1845G
| Category: | POP , Polyolefin Plastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | AFFINITY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RMdXN9_AFFINITY-PL-1845G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AFFINITY™ PL 1845G Polyolefin Plastomer is a Polyolefin Plastomer (POP) produced using INSITE™ Technology from Dow Plastics. It is specifically designed for use as a sealant layer in flexible structures prepared using the cast process. Its low heat seal initiation temperature, its outstanding optical properties and its coextrusion capability with polypropylene polymers make AFFINITY PL 1845G Polyolefin Plastomer the ideal resin for use as low temperature sealing skin layer in coextruded cast bioriented polypropylene (BOPP) film structures. AFFINITY PL 1845G Polyolefin Plastomer does not contain any slip nor antiblock agent. In order to optimise the application performance, it is recommended to add slip/antiblock master batches based on polyolefin plastomers. Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.910 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.5 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D882 | ||
| MD : Break, 25 µm, Cast Film | 45.0 | MPa | |
| TD : Break, 25 µm, Cast Film | 33.0 | MPa | |
| Tensile Elongation 2 | ASTM D882 | ||
| MD : Break, 25 µm, Cast Film | 530 | % | |
| TD : Break, 25 µm, Cast Film | 670 | % | |
| Dart Drop Impact 3(25 µm, Cast Film) | 470 | g | ASTM D1709B |
| Elmendorf Tear Strength 4 | ASTM D1922 | ||
| MD : 25 µm, Cast Film | 180 | g | |
| TD : 25 µm, Cast Film | 360 | g | |
| Seal Initiation Temperature | Internal Method | ||
| 20 µm 5 | 95.0 | °C | |
| 25 µm, Cast Film 6 | 99.0 | °C |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 95.0 | °C | ISO 306/A |
| Melting Temperature | 103 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 20°, 20.0 µm 7 | 96 | ||
| 20°, 25.0 µm, Cast Film 8 | 145 | ||
| Clarity 9(25.0 µm, Cast Film) | 75.0 | ASTM D1746 | |
| Haze | ASTM D1003 | ||
| 20.0 µm 10 | 1.2 | % | |
| 25.0 µm, Cast Film 11 | 0.70 | % |
| Note Message | |
|---|---|
| 1 . | Single layer cast film, extruded at 274 °C , 0.5 mm die gap. |
| 2 . | Single layer cast film, extruded at 274 °C , 0.5 mm die gap. |
| 3 . | Single layer cast film, extruded at 274 °C , 0.5 mm die gap. |
| 4 . | Single layer cast film, extruded at 274 °C , 0.5 mm die gap. |
| 5 . | BOPP Film; 1 µm sealant layer each sideTemperature at which 1.8 N/15 mm heat seal strength is reached |
| 6 . | Single layer cast film, extruded at 274 °C , 0.5 mm die gap.Temperature required to reach 5.25 N/15 mm heat seal strength |
| 7 . | BOPP Film; 1 µm sealant layer each side |
| 8 . | Single layer cast film, extruded at 274 °C , 0.5 mm die gap. |
| 9 . | Single layer cast film, extruded at 274 °C , 0.5 mm die gap. |
| 10 . | BOPP Film; 1 µm sealant layer each side |
| 11 . | Single layer cast film, extruded at 274 °C , 0.5 mm die gap. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PC GN1007FT | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| WPP PP PPH3MG3.5-Black | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| Delrin® 300PE NC010 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| Fluoroplex B 60 - GMA | UNIFLON | PTFE | Fluoroplex |
| EMOPLEN® HP MTF 5 | EMAS Plastik San.Tic.AS. | PP Homopolymer | EMOPLEN® |