SCHULADUR® E GF 50 SCHWARZ
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULADUR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RMYklA_SCHULADUR-E-GF-50-SCHWARZ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 50% glass fibre reinforced PET-grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.79 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 15.0 | cm³/10min | ISO 1133 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 20000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 195 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 17000 | MPa | ISO 178 |
| Flexural Stress 2 | 290 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 45 | kJ/m² | ISO 179/1eU |
| 23°C | 50 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 250 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 233 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 247 | °C | ISO 306/A50 |
| -- | 235 | °C | ISO 306/B50 |
| Ball Pressure Test (200°C) | Pass | IEC 60695-10-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (2.00 mm) | 20 | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 1.50 mm | HB | IEC 60695-11-10, -20 | |
| 3.00 mm | HB | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 700 | °C | IEC 60695-2-12 |
| 3.00 mm | 800 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 725 | °C | IEC 60695-2-13 |
| 3.00 mm | 825 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AZR-Ecoplast 143 HDPE black 0.5 | UrbanPlast SIA | HDPE | AZR-Ecoplast |
| DIAREX® H350E | PTT Global Chemical Public Company Limited | PS (HIPS) | DIAREX® |
| Geon™ Vinyl Flexible 90072 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| TEDUR® L 9406-1 | ALBIS PLASTIC GmbH | PPS | TEDUR® |
| Comco PA6G GLASS | Comco Nylon GmbH | Nylon 6 | Comco |