GLS Nylon 66 LKG36
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | GLS Polymers Pvt. Ltd. |
| Trademark: | GLS Nylon 66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RMRGNt_GLS-Nylon-66-LKG36.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylon66 15 PTFE 30 GF Precolor |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 to 1.24 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.5 to 3.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | > 2800 | MPa | ASTM D638 |
| Tensile Strength 1(Yield) | > 66.0 | MPa | ASTM D638 |
| Flexural Modulus | > 2400 | MPa | ASTM D790 |
| Flexural Strength | > 96.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | > 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 76.0 to 80.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 275 to 298 | °C | |
| Mold Temperature | 67.0 to 106 | °C | |
| Injection Pressure | 68.0 to 128 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AFLAS® 150P | Asahi Glass Co., Ltd. | Fluorelastomer | AFLAS® |
| Gallonprene® GP420-3002 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Gebalon 10-141 HI | geba Kunststoffcompounds GmbH | PC | Gebalon |
| ELASTOSIL® N 9111 WHITE | Wacker Chemie AG | Silicone | ELASTOSIL® N |
| OmniLon™ PA6/6 U IM8 | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |