Zytel® 70G30HSLR NC010

Category:	Nylon 66 , NYLON RESIN
Manufacturer:	DuPont Performance Polymers
Trademark:	Zytel®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	RLnVQL_Zytel70G30HSLRNC010.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
30% Glass Reinforced, Heat Stabilized, Hydrolysis Resistant, Polyamide 66

General Information
Filler / Reinforcement	Glass fiber reinforced material, 30% filler by weight
Additive	heat stabilizer Lubricant demoulding
Features	Hydrolysis resistance Thermal Stability
RoHS Compliance	Contact manufacturer
Forms	Particle
Processing Method	Injection molding
Multi-Point Data	Coefficient of Thermal Expansion vs. Temperature (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature, Dynamic (ISO 11403-1) Shear Stress vs. Shear Rate (ISO 11403-1) Tensile Fatigue (Wöhler) (ISO 11403-2) Tensile Modulus vs. Temperature, Dynamic (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)
Part Marking Code (ISO 11469)	>PA66-GF30
Resin ID (ISO 1043)	PA66-GF30

Physical	Dry	Conditioned	Unit	Test Method
Density	1.37	--	g/cm³	ISO 1183
Molding Shrinkage				ISO 294-4
Transverse flow	1.1	--	%	ISO 294-4
Flow	0.30	--	%	ISO 294-4
Water Absorption				ISO 62
Saturated, 23°C, 2.00mm	6.0	--	%	ISO 62
Balance, 23°C, 2.00mm, 50% RH	1.9	--	%	ISO 62

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus	10000	7000	MPa	ISO 527-2
Tensile Stress (Break)	200	130	MPa	ISO 527-2
Tensile Strain (Break)	3.3	5.0	%	ISO 527-2
Tensile Creep Modulus				ISO 899-1
1 hr	--	6800	MPa	ISO 899-1
1000 hr	--	5100	MPa	ISO 899-1

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179/1eA
-30°C	10	10	kJ/m²	ISO 179/1eA
23°C	13	15	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength				ISO 179/1eU
-30°C	70	70	kJ/m²	ISO 179/1eU
23°C	80	90	kJ/m²	ISO 179/1eU
Notched Izod Impact				ISO 180/1A
-30°C	12	10	kJ/m²	ISO 180/1A
23°C	12	14	kJ/m²	ISO 180/1A

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	261	--	°C	ISO 75-2/B
1.8 MPa, not annealed	253	--	°C	ISO 75-2/A
Glass Transition Temperature ¹	80.0	20.0	°C	ISO 11357-2
Vicat Softening Temperature	250	--	°C	ISO 306/B50
Melting Temperature ²	262	--	°C	ISO 11357-3
Linear thermal expansion coefficient				ISO 11359-2
Flow	2.6E-5	--	cm/cm/°C	ISO 11359-2
Flow : -40 to 23°C	2.6E-5	--	cm/cm/°C	ISO 11359-2
Flow : 55 to 160°C	1.3E-5	--	cm/cm/°C	ISO 11359-2
Lateral	8.0E-5	--	cm/cm/°C	ISO 11359-2
Horizontal : -40 to 23°C	7.0E-5	--	cm/cm/°C	ISO 11359-2
Horizontal : 55 to 160°C	1.3E-4	--	cm/cm/°C	ISO 11359-2
Effective Thermal Diffusivity	1.10E-7	--	m²/s

Flammability	Dry	Conditioned	Unit	Test Method
FMVSS Flammability	SE/B	--		FMVSS 302
Fogging				ISO 6452
F-value (refraction)	95	--	%	ISO 6452
G-value (condensate)	3.0E-4	--	g	ISO 6452

Fill Analysis	Dry	Conditioned	Unit	Test Method
Specific Heat Capacity of Melt	2290	--	J/kg/°C
Thermal Conductivity of Melt	0.21	--	W/m/K

Additional Information	Dry	Conditioned	Unit	Test Method
Emission of Organic Compounds	3.20	--	µgC/g	VDA 277
Odor	4.50	--		VDA 270
Thermal Desorption Analysis of Organic Emissions	5.00	--	µg/g	VDA 278

Injection	Dry	Unit
Melt Temperature, Optimum	295	°C
Mold Temperature, Optimum	100	°C
Drying Recommended	yes
Hold Pressure Time	3.00	s/mm
Maximum Screw Tangential Speed	200	mm/sec

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	--	1.0E+13	ohms	IEC 60093
Volume Resistivity	> 1.0E+15	1.0E+11	ohms·cm	IEC 60093
Dielectric Strength	38	32	kV/mm	IEC 60243-1
Relative Permittivity				IEC 60250
100 Hz	4.30	11.0		IEC 60250
1 MHz	4.10	4.60		IEC 60250
Dissipation Factor				IEC 60250
100 Hz	7.0E-3	0.46		IEC 60250
1 MHz	0.015	0.065		IEC 60250
Comparative Tracking Index (CTI) (3.00 mm)	PLC 1	--		UL 746
Comparative Tracking Index	450	--	V	IEC 60112

Flammability	Dry	Conditioned	Unit	Test Method
Burning Rate ³(1.00 mm)	24	--	mm/min	ISO 3795
Flame Rating				UL 94, IEC 60695-11-10, -20
0.75 mm	HB	--		UL 94, IEC 60695-11-10, -20
1.5 mm	HB	--		UL 94, IEC 60695-11-10, -20
Oxygen Index	24	--	%	ISO 4589-2

Fill Analysis	Dry	Conditioned	Unit	Test Method
Melt Density	1.20	--	g/cm³
Ejection Temperature	210	--	°C

Injection	Dry	Unit
Drying Temperature	80	°C
Drying Time - Desiccant Dryer	2.0 - 4.0	hr
Suggested Max Moisture	0.20	%
Processing (Melt) Temp	285 - 305	°C
Mold Temperature	70 - 120	°C
Holding Pressure	50.0 - 100	MPa

Note Message
1 .	10°C/min
2 .	10°C/min
3 .	FMVSS 302

Resin Grade	Manufacturer	Category	Trademark
SUMIPEX® HT20Y	Sumitomo Chemical Co., Ltd.	Acrylic (PMMA)	SUMIPEX®
Monprene® IN-19147	Teknor Apex Company	TPE	Monprene®
FHR Polypropylene P4C5B-076	Flint Hills Resources, LP	PP Homopolymer	FHR Polypropylene
INSTRUC PPGF20CC	Infinity LTL Engineered Compounds	PP, Unspecified	INSTRUC
LUVOCOM® 1-8501	LEHVOSS Group	Nylon 66	LUVOCOM®