Sarlink® TPE AB-1246DN
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RKlmWG_Sarlink-TPE-AB-1246DN.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sarlink®TPE AB-1246DN is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is injection molding. Sarlink®The typical application field of TPE AB-1246DN is: automobile industry |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.898 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.6 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.4 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 10 sec) | 46 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 315 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 14.7 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 22 | % | ASTM D412 |
| Tear Strength 2 | 77.1 | kN/m | ASTM D1004 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength (110°C, 1000 hr) | 4.9 | % | ASTM D471 |
| Change in Ultimate Elongation (110°C, 1000 hr) | 5.3 | % | ASTM D471 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -65.0 | °C | ASTM D746 |
| Additional Information |
|---|
| 可燃性燃烧速率，最大100 (FMVSS 302) 合格 (0.82英寸/分钟)热变形，0.45兆帕 (64 PSI)= 58热变形，1.82兆帕 (264 PSI)= 39CLTE， 平行于流体1.47X10E-8 毫米/毫米/CCLTE， 平行于流体1.32X10E-8 毫米/毫米/C雾化3小时，100°C，冷却板 21°C，1小时后的试验值 (SAE-J1756) = 92雾化3小时，100°C，冷却板 21°C，16小时后的试验值 (SAE-J1756) = 92 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 199 - 210 | °C | |
| Middle Temperature | 204 - 216 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Nozzle Temperature | 216 - 227 | °C | |
| Processing (Melt) Temp | 216 - 227 | °C | |
| Mold Temperature | 35.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 120 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| 无需干燥。但如果湿度过大，则将粒料在150°F (65°C)的温度下干燥2-4小时。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 193 - 204 | °C | |
| Cylinder Zone 2 Temp. | 199 - 210 | °C | |
| Cylinder Zone 3 Temp. | 204 - 216 | °C | |
| Cylinder Zone 5 Temp. | 210 - 221 | °C | |
| Die Temperature | 216 - 227 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propylux® HS2 | Westlake Plastics Company | PP, Unspecified | Propylux® |
| Argothane® ST-2592-90 | Argotec LLC | TPU, Unspecified | Argothane® |
| Geon™ Vinyl Wire & Cable WJKC302R | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |
| RTP 1899 X 141361 NAT/CLEAR | RTP Company | Acrylic (PMMA) | RTP |
| ADENE® O07MJBGD00 | A.D. Compound S.p.A. | PP Copolymer | ADENE® |