POM GRIS 8109 is a polyoxymethylene for injection molding. POM GRIS 8109 is used for injection molding applications in the automotive engineering and electrical industries. Moreover, it is available in a large variety of colors to answer the requests of the various markets. |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.65 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 144 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 32.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 9.0 | % | ISO 527-2/50 |
| Flexural Modulus | 2700 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 67.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 5.5 | kJ/m² | |
| 23°C | 5.5 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 104 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 151 | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 166 | °C | ISO 3146 |
| CLTE - Flow (23 to 80°C) | 1.2E-4 | cm/cm/°C | DIN 52328 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric Strength | 35 | kV/mm | IEC 60243-1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 190 to 210 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Injection Pressure | 60.0 to 200 | MPa | |
| Back Pressure | 0.00 to 2.00 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAKETON GF 15 | A. Schulman Europe | PK-Aliphatic | SCHULAKETON |
| AEI TP-0840 | AEI Compounds Limited | PE, Unspecified | AEI |
| Altuglas® MI-8E | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Altuglas® |
| Karina YELLOW PVC COMPOUND 813D02/28-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lucent PP TPP-140 | Lucent Polymers, Inc. | PP Homopolymer | Lucent PP |