Tipwood® 50 EX

Category:	PP Copolymer , Polypropylene Copolymer
Manufacturer:	Tipco Industries Ltd.
Trademark:	Tipwood®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	RIspuW_Tipwood-50-EX.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Tipwood® 50 EX is a Wood-Fibre Reinforced, Heat Stabilized Polypropylene Compound specially developed by Tipco for Automobile Interiors and Appliance Fascia Applications

Features:

Environmentally Friendly Material

Easy Recyclability

45-50% Special Wood Filler

Excellent Extrudability

High Melt Strength

Superior Draw Down for Vacuum / Thermo Formability

Wood-Like Surface Aesthetics

Good Izod Impact Strength

High Stiffness & Good Durability

Good Sound Barrier Properties

Extremely Low Thermal Sag

Applications:
Sheet Extrusion, Thermoforming, Profiles, Blow Moulding and Lamination.
Automotive Car Interiors, Door Panels, Trims, Wood-Finish Panels, Office Files, Trays, Marine Flooring, Audio Speakers, Resonator Devices, Blow Moulded Bottles, Furniture, Mono-Block Chairs and various Artificial Wood Products.

General Information
Filler / Reinforcement	Wood Fiber
Additive	Heat Stabilizer
Features	Copolymer Durable Environmentally Sound Good Impact Resistance Good Melt Strength High Stiffness Sound Damping
Uses	Appliance Components Automotive Interior Parts Automotive Interior Trim Fascias Furniture Profiles
Forms	Pellets
Processing Method	Blow Molding Sheet Extrusion Thermoforming

Physical	Nominal Value	Unit	Test Method
Density	1.08	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (230°C/10.0 kg)	6.0	g/10 min	ASTM D1238
Molding Shrinkage - Flow	0.80	%	ASTM D955
Moisture Content	0.25	%	ASTM D817

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield)	24.5	MPa	ASTM D638
Tensile Elongation (Break)	8.0	%	ASTM D638
Flexural Modulus	2450	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	34	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	92.0	°C	ASTM D648

Extrusion	Nominal Value	Unit
Drying Temperature	80.0 to 90.0	°C
Drying Time	5.0 to 7.0	hr
Melt Temperature	< 225	°C

Resin Grade	Manufacturer	Category	Trademark
Miramid® VEP30C	BASF Leuna GmbH	Nylon 6	Miramid®
TRIBOCOMP® A-3 TS0	EPIC Polymers	Nylon 66	TRIBOCOMP®
Nanjing Hongrui PP P860	Nanjing Hongrui Engineering Plastics Co., Ltd.	PP, Unspecified	Nanjing Hongrui PP
LNP™ LUBRICOMP™ DX96651 compound	SABIC Innovative Plastics	PC	LNP™ LUBRICOMP™
OmniTech™ PET GR30	OMNI Plastics, LLC	PET	OmniTech™