Borealis PP BD020AIB
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RIH2SR_Borealis-PP-BD020AIB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BD020AIB is a polypropylene compound intended for injection moulding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.890 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 24.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 1100 | MPa | ISO 178 |
| Flexural Stress | 30.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 6.0 | kJ/m² | ISO 179 |
| 23°C | 16 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 80.0 | °C | ISO 75-2/Be |
| 1.8 MPa, not annealed | 50.0 | °C | ISO 75-2/Ae |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability | mm/min | ISO 3795 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Feeding Temperature: 40 to 80 °CMass Temperature: 220 to 260 °CBack Pressure: Low to MediumSrew Speed: Low to MediumFlow Front Speed: 100 to 200 mm/s |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toyolac® 430Y MH1 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| NEO-ZEX™ 0234N | Prime Polymer Co., Ltd. | LLDPE | NEO-ZEX™ |
| NILFLEX® SH A0 MN001 | Taro Plast S.p.A. | SEBS | NILFLEX® |
| Ecovio® F2223 | BASF Corporation | Copolyester | Ecovio® |
| Hifax TRC 221P | LyondellBasell Industries | PP Copolymer | Hifax |