POLYREX® PH-60
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | CHI MEI CORPORATION |
| Trademark: | POLYREX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RHgoz6_POLYREX-PH-60.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYREX® PH-60 is a High Impact Polystyrene product. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 5.5 | g/10 min | |
| 220°C/10.0 kg | 16 | g/10 min | |
| Melt Volume-Flow Rate (MVR) (200°C/5.0 kg) | 5.50 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 75 | ASTM D785 | |
| Ball Indentation Hardness (H 358/30) | 90.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Yield | 27.0 | MPa | ISO 527-2/50 |
| Break | 27.0 | MPa | ISO 527-2/50 |
| 3.00 mm 1 | 28.4 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Break, 3.00 mm 2 | 40 | % | ASTM D638 |
| Break | 64 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 6.00 mm 3 | 2160 | MPa | ASTM D790 |
| -- 4 | 1600 | MPa | ISO 178 |
| Flexural Strength | |||
| 6.00 mm 5 | 42.2 | MPa | ASTM D790 |
| -- 6 | 40.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 8.0 | kJ/m² | ISO 179, ISO 179/2C |
| Charpy Unnotched Impact Strength | 110 | kJ/m² | ISO 179/2U |
| Notched Izod Impact | |||
| 23°C, 3.00 mm | 83 | J/m | ASTM D256 |
| 23°C, 6.00 mm | 74 | J/m | ASTM D256 |
| -- | 7.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 81.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 78.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 96.0 | °C | ASTM D648 |
| 1.8 MPa, Annealed | 94.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 100 | °C | ASTM D1525, ISO 306/A50 6 7 |
| -- | 104 | °C | ISO 306/A120 |
| -- | 92.0 | °C | ISO 306/B50 |
| -- | 99.0 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | HB | ||
| 1.60 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 150 to 170 | °C | |
| Middle Temperature | 175 to 195 | °C | |
| Front Temperature | 180 to 200 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 6.0 mm/min |
| 2 . | 6.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Rate A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 5132-75UV Clear Pink 6277 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 5145-70 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Plaslube® POM HO CF10 TL20 | Techmer Engineered Solutions | Acetal (POM) Homopolymer | Plaslube® |
| HI-ZEX MILLION™ 030S | Mitsui Chemicals, Inc. | HMWPE | HI-ZEX MILLION™ |
| ALTECH® PBT + ASA A 2020/510 GF20 | ALBIS PLASTIC GmbH | PBT+ASA | ALTECH® PBT + ASA |