ENGAGE™ 8157
| Category: | TPO (POE) , Polyolefin Elastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ENGAGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RGm3W6_ENGAGE-8157.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ENGAGE™8157 polyolefin elastomer is an ethylene-octene copolymer with excellent flow properties. After blending with polypropylene (PP) and polyethylene (PE), the product has particularly excellent impact resistance and is widely used in TPO applications requiring excellent low-temperature impact resistance. ENGAGE 8157 has high filler content and excellent peroxide curing performance. After being cured by peroxide, silane and irradiation, the product has excellent thermal aging properties, compression deformation and weather resistance, and may be used in the manufacture of high-performance electrical insulation products. Main features:
Application field:
|
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.868 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Mooney Viscosity (ML 1+4, 121°C) | 33 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 1 second, molded | 70 | ASTM D2240 | |
| Shore D, 1 second, molded | 20 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant 1(Compression Molded) | 2.60 | MPa | ASTM D638 |
| Tensile Strength 2(Break, Compression Molded) | 9.50 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Compression Molded) | 810 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% secant : Molding | 15.2 | MPa | ASTM D790 |
| 2% secant : Molding | 14.4 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 4 | 37.3 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -52.0 | °C | Internal method |
| Vicat Softening Temperature | 46.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) 5 | 55.0 | °C | Internal method |
| Peak Crystallization Temperature (DSC) | 42.0 | °C | Internal method |
| Additional Information |
|---|
| 对无滑石粉产品测量的属性。 |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| 4 . | C mould |
| 5 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravaflex SBR 1502 | Ravago Group | SBR, Unspecified | Ravaflex |
| SCANAMID 66 A13^ FX30 | Polykemi AB | Nylon 66 | SCANAMID 66 |
| TRIREX® 3022A | Samyang Corporation | PC | TRIREX® |
| VALOX™ 7062HP resin | SABIC Innovative Plastics Asia Pacific | PBT | VALOX™ |
| POLIMAXX 1111NXTA4 | IRPC Public Company Limited | PP Homopolymer | POLIMAXX |