Order Products : sales@su-jiao.com
ForTii® LDS51
| Category: | Nylon 4T , Polyamide 4T |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | ForTii® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RFx6As_ForTiiLDS51.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ForTii®LDS51 is a Polyamide 4T (Nylon 4T) material, which contains a 30% glass fiber reinforced material. This product is available in North America, Europe or Asia Pacific region. The processing method is injection molding. ForTii®The main features of LDS51 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.58 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 1.0 | -- | % | ISO 294-4 |
| Flow | 0.30 | -- | % | ISO 294-4 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 11000 | 11000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 120 | 120 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.6 | 1.6 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 25 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 290 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 325 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow | 3.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral | 4.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | > 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 400 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification (0.8 mm) | V-0 | -- | IEC 60695-11-10, -20 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 - 8.0 | hr | |
| Rear Temperature | 320 - 330 | °C | |
| Middle Temperature | 325 - 335 | °C | |
| Front Temperature | 330 - 335 | °C | |
| Nozzle Temperature | 330 - 335 | °C | |
| Processing (Melt) Temp | 330 - 340 | °C | |
| Mold Temperature | 100 - 150 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.500 - 3.00 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AVALON® 75 AE | Huntsman Corporation | TPU-Polyester | AVALON® |
| Fainplast PVC R 218 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Gallonprene® GP420-5503 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Magnobond 3347 | Magnolia Plastics, Inc. | Epoxy | Magnobond |
| PENTAMID B GV30 E8 H natur | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |