Lusep® SP2300
| Category: | SPS , Syndiotactic Polystyrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lusep® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RE0YSg_Lusep-SP2300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description General purpose Application Pump Units, Pick-up Lends Holder, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 to 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break, 3.20 mm) | 118 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 2.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 8830 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 177 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 88 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm 5 | 260 | °C | |
| 0.45 MPa, Unannealed, 6.40 mm 6 | 220 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (23°C, 1.00 mm) | 35 | kV/mm | ASTM D149 |
| Comparative Tracking Index (Solution A) | 500 to 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Rear Temperature | 270 to 290 | °C | |
| Middle Temperature | 280 to 310 | °C | |
| Front Temperature | 290 to 310 | °C | |
| Nozzle Temperature | 280 to 310 | °C | |
| Processing (Melt) Temp | 280 to 310 | °C | |
| Mold Temperature | 80.0 to 150 | °C | |
| Screw Speed | 40 to 80 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 4.6kg |
| 6 . | 18.6kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Restramid PA 6.6 30GF | Polimarky Spolka Jawna | Nylon 66 | Restramid |
| SILPURAN® 8020/40 | Wacker Chemie AG | Silicone | SILPURAN® |
| INNOPOL® PP CS 1-2140 LH | Inno-Comp Ltd. | PP Homopolymer | INNOPOL® PP |
| Jampilen HP515M | Jam Polypropylene Company | PP Homopolymer | Jampilen |
| PLUSTEK RA116 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |