Ultramid® 1503-2 NF2004
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RDavd9_Ultramid-1503-2-NF2004.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultramid 1503-2 NF2004 is a 33% glass reinforced, heat stabilized injection molding PA6/6. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.40 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | -- | % | |
| Water Absorption | ||||
| Saturation | 5.7 | -- | % | ASTM D570 |
| Saturation, 23°C | 5.7 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 1.7 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.7 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 10800 | 7400 | MPa | ISO 527-2 |
| Tensile Strength | ||||
| Break, 23°C | 193 | -- | MPa | ASTM D638 |
| Break, 23°C | 210 | 145 | MPa | ISO 527-2 |
| Tensile Elongation | ||||
| Break, 23°C | 3.0 | -- | % | ASTM D638 |
| Break, 23°C | 3.0 | 5.0 | % | ISO 527-2 |
| Flexural Modulus | ||||
| 23°C | 8280 | -- | MPa | ASTM D790 |
| 23°C | 9900 | 6300 | MPa | ISO 178 |
| Flexural Strength (23°C) | 276 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 11 | 11 | kJ/m² | |
| 23°C | 12 | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 75 | 75 | kJ/m² | |
| 23°C | 90 | 100 | kJ/m² | |
| Notched Izod Impact | ||||
| 23°C | 120 | -- | J/m | ASTM D256 |
| 23°C | 11 | 15 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 297 | -- | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 264 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 252 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 255 | -- | °C | ISO 75-2/A |
| Peak Melting Temperature | 260 | -- | °C | ASTM D3418, ISO 3146 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 1.0 to 2.0 | hr | |
| Suggested Max Moisture | 0.040 to 0.20 | % | |
| Processing (Melt) Temp | 288 to 305 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 to 0.350 | MPa | |
| Screw Speed | 40 to 80 | rpm | |
| Screw Compression Ratio | 3.0:1.0 to 4.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6 7400 GK 15 UV | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| Vinylbond 95-950-60 | Colorite Polymers | PVC, Flexible | Vinylbond |
| Hanwha Total PP HF409 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| ESTADIENE 1016 HT V0 | Cossa Polimeri S.r.l. | ABS | ESTADIENE |
| Infino NH-1015 | SAMSUNG SDI CO., LTD. | PC+ABS | Infino |