LNP™ THERMOCOMP™ DF004RXP compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RD4e7D_LNP-THERMOCOMP-DF004RXP-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP DF004RXP is a compound based on Polycarbonate resin containing 20% Glass Fiber. Some light color grades may have lower impact data than natural and black. Added features include: Mold Release, UL Also known as: LNP* THERMOCOMP* Compound DF004RXP Product reorder name: DF004RXP |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.20 - 0.40 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.60 - 0.80 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.13 | % | ASTM D570 |
| 23°C, 24 hr | 0.17 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6100 | MPa | ASTM D638 |
| -- | 5730 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 105 | MPa | ASTM D638 |
| Yield | 105 | MPa | ISO 527-2/5 |
| Fracture 3 | 102 | MPa | ASTM D638 |
| Fracture | 104 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.9 | % | ASTM D638 |
| Yield | 3.1 | % | ISO 527-2/5 |
| Fracture 5 | 3.3 | % | ASTM D638 |
| Fracture | 3.4 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 6 | 6070 | MPa | ASTM D790 |
| -- 7 | 5890 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 163 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 173 | MPa | ASTM D790 |
| Fracture, 50.0mm span 9 | 169 | MPa | ASTM D790 |
| Flexural Strain at Break 10 | 3.7 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C, Light & White Colors | 98 | J/m | ASTM D256 |
| 23°C, Natural & Black Colors | 130 | J/m | ASTM D256 |
| 23°C 11 | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 900 | J/m | ASTM D4812 |
| 23°C 12 | 53 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 24.5 | J | ASTM D3763 |
| -- | 5.08 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 141 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 13 | 141 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow : -30 to 30°C | 2.9E-5 | cm/cm/°C | ASTM D696 |
| Lateral : -30 to 30°C | 5.4E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.750 to 3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 3.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 260 - 280 | °C | |
| Middle Temperature | 270 - 290 | °C | |
| Front Temperature | 280 - 300 | °C | |
| Nozzle Temperature | 285 - 305 | °C | |
| Processing (Melt) Temp | 285 - 310 | °C | |
| Mold Temperature | 80.0 - 110 | °C | |
| Back Pressure | 0.100 - 0.300 | MPa | |
| Screw Speed | 50 - 90 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 2 mm/min |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3838 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Shin-Etsu Elastomer SV-16000U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| 4PROP® 9C13100 | 4Plas | PP Copolymer | 4PROP® |
| INEOS PP H05H-01 | INEOS Olefins & Polymers USA | PP Homopolymer | INEOS PP |
| Sylvin 9604-95C CLEAR | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |