INSULCAST® RTVS 3-95-2
| Category: | Silicone Rubber, RTV-2 , Silicone Rubber, RTV-2 |
| Manufacturer: | ITW Polymers Coatings North America |
| Trademark: | INSULCAST® RTVS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RCZzhz_INSULCAST-RTVS-3-95-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| INSULCAST RTVS 3-95-2 is a very highly thermally conductive, high temperature RTV silicone compound which meets the flammability requirements of UL 94V-0. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 85 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 2.76 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 17 | % | ASTM D412 |
| Tear Strength 1 | 0.876 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow | 1.5E-4 | cm/cm/°C | |
| Thermal Conductivity | 1.4 | W/m/K | ASTM D5470 |
| Service Temperature | -55 to 260 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | ASTM D257 | ||
| 25°C | 1.0E+14 | ohms·cm | |
| 125°C | 1.0E+13 | ohms·cm | |
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 5.00 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 5.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Volume: 1.0 Mix Ratio by Weight: 1.0 | ||
| Part B | Mix Ratio by Volume: 1.0 Mix Ratio by Weight: 1.0 | ||
| Shelf Life (25°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 2 | Clear/Transparent | ||
| -- 3 | Red | ||
| Density | |||
| -- 4 | 2.26 | g/cm³ | |
| -- 5 | 2.35 | g/cm³ | |
| Viscosity | ASTM D2393 | ||
| -- 6 | 35 | Pa·s | |
| 25°C 7 | 35 | Pa·s | |
| 25°C 8 | 35 | Pa·s | |
| Curing Time | |||
| 125°C | 0.25 | hr | |
| 90°C | 1.0 | hr | |
| 65°C | 2.0 to 4.0 | hr | |
| 25°C | 24 | hr | |
| Gel Time (25°C) | 1.2E+2 to 2.4E+2 | min | |
| Pot Life (25°C) | 90 | min |
| Note Message | |
|---|---|
| 1 . | Die B |
| 2 . | Part B |
| 3 . | Part A |
| 4 . | Part B |
| 5 . | Part A |
| 6 . | Mixed |
| 7 . | Part B |
| 8 . | Part A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 D AR 10 TFE 5 | RTP Company | Nylon 612 | RTP |
| Synres® SR-1209A | Teknor Apex Company | PP, Unspecified | Synres® |
| EGYPTENE HD 5218 EA | Sidpec (Sidi Kerir Petrochemicals Co.) | HDPE | EGYPTENE |
| Karina GREEN PVC COMPOUND 852-40/5-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plaslube® PA6/6 CF33 ML2 BK | Techmer Engineered Solutions | Nylon 66 | Plaslube® |