SURPASS® FPs417-A
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | NOVA Chemicals |
| Trademark: | SURPASS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RCMIYy_SURPASS-FPs417-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SURPASS®FPs417-A is a linear low density polyethylene material,. This product is available in North America and is processed by film extrusion or co-extrusion. SURPASS®The main features of the FPs417-A are:
Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.917 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.4 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 20 µm, cast film | 100 | MPa | ASTM D882 |
| 1% secant, TD : 20 µm, cast film | 120 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 20 µm, extruded film | 7.50 | MPa | ASTM D882 |
| TD : Yield, 20 µm, extruded film | 7.00 | MPa | ASTM D882 |
| MD : Fracture, 20 µm, extruded film | 32.0 | MPa | ASTM D882 |
| TD : Fracture, 20 µm, extruded film | 25.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 20 µm, extruded film | 470 | % | ASTM D882 |
| TD : Fracture, 20 µm, extruded film | 780 | % | ASTM D882 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20 µm, cast film | 380 | g | ASTM D1922 |
| TD : 20 µm, cast film | 540 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 20.0 µm, Cast Film) | 85 | ASTM D2457 | |
| Haze (20.0 µm, Cast Film) | 0.80 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Low Friction Puncture - Cast Film (20.0 µm) | 830 | J/cm | Internal method |
| Ultimate Elongation - Cast Film (20.0 µm) | 360 | % | Internal method |
| Film properties are typical of cast film extruded at a melt temperature of 500°F, and a line speed of 800 ft/min. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UBESTA 3035 LU1 | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| ESTASAN SAN 3000 | Cossa Polimeri S.r.l. | SAN | ESTASAN |
| LEXAN™ HFD1930 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| LNP™ KONDUIT™ DTK22 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ KONDUIT™ |
| LUVOCOM® 80/TF/18/SI/2 - 1P | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |