Kingfa PA66-G50
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RBrLX3_Kingfa-PA66-G50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa PA66-G50 is a polyamide 66 (nylon 66) material, which contains a 50% glass fiber reinforced material. This product is available in North America or Asia Pacific region. The processing method is injection molding. The main features of Kingfa PA66-G50 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.56 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 23°C | 0.20 | % | ASTM D955 |
| Transverse flow : 23°C | 0.70 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.60 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 210 | MPa | ASTM D638 |
| Flexural Modulus 2 | 13000 | MPa | ASTM D790 |
| Flexural Strength 3 | 300 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 258 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 253 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 110 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 260 - 280 | °C | |
| Middle Temperature | 265 - 300 | °C | |
| Front Temperature | 275 - 305 | °C | |
| Processing (Melt) Temp | 275 - 310 | °C | |
| Mold Temperature | 50.0 - 80.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Processing Temperature Limit: 310°C |
| Note Message | |
|---|---|
| 1 . | 10 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MEGOLON™ + S800 | AlphaGary | TP, Unspecified | MEGOLON™ |
| SCHULAMID® 612 GF33 | A. Schulman Europe | Nylon 612 | SCHULAMID® |
| PLUSTEK PA301G50 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |
| Sylvin 9600-50 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| POCAN® T 7331 POS151 700226 | LANXESS GmbH | PBT+PET | POCAN® |