DOWLEX™ NG 2429.01G
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RAeam5_DOWLEX-NG-2429-01G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
DOWLEX™ NG 2429.01G Polyethylene Resin is an ethylene octene copolymer for rotational moulding and is specifically designed for applications requiring excellent environmental stress crack resistance and impact strength combined with low warpage and good processing. DOWLEX NG 2429.01G is fully heat and UV stabilized resulting in a wide processing latitude, good colour retention, and long life expectancy. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.935 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance | ASTM D1693 | ||
| 50°C, 10% Antarox, Rotational Molded 1 | 400 | hr | |
| 50°C, 100% Antarox, Compression Molded | > 1000 | hr |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 57 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield, Compression Molded | 17.0 | MPa | |
| Yield, Rotational Molded 2 | 17.0 | MPa | |
| Break, Compression Molded | 24.7 | MPa | |
| Break, Rotational Molded 3 | 21.8 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Break, Compression Molded | 800 | % | |
| Break, Rotational Molded 4 | 700 | % | |
| Flexural Modulus - 1% Secant (Compression Molded) | 640 | MPa | ISO 178 |
| Tear Resistance | DIN 53515 | ||
| -- 5 | 140 | MPa | |
| Compression Molded | 145 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | ||
| -20°C, 1.00 mm, Compression Molded | 23.0 | J | |
| 23°C, Rotational Molded 6 | 17.0 | J | |
| 23°C, 1.00 mm, Compression Molded | 17.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 38.9 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 118 | °C | ISO 306/A120 |
| Melting Temperature | 125 | °C | DSC |
| Peak Crystallization Temperature (DSC) | 105 | °C | DSC |
| Note Message | |
|---|---|
| 1 . | 3 to 4 mm plate thickness |
| 2 . | 3 to 4 mm plate thickness |
| 3 . | 3 to 4 mm plate thickness |
| 4 . | 3 to 4 mm plate thickness |
| 5 . | Rotational Molded, 3 to 4 mm plate thickness |
| 6 . | 3 to 4 mm plate thickness |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Centrene® HDF193N | Qenos Pty Ltd | HDPE, HMW | Centrene® |
| ESTAPROP 1040 V2 HK BLU 6237 PANT 285C | Cossa Polimeri S.r.l. | PP Copolymer | ESTAPROP |
| Electrafil® TPU 95A CF15 | Techmer Engineered Solutions | TPU, Unspecified | Electrafil® |
| SABIC® LLDPE 218BJ | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |
| Sylvin 5132-86 Clear Green 3164 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |