VALOX™ V8030CS resin
| Category: | PBT+PET , Polybutylene Terephthalate + PET |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R9aHbi_VALOX-V8030CS-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Dual processable for use in cooking appliance components such as gas-assist molded handles and injection molded end caps |
| General Information | |
|---|---|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183, ASTM D792 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 265°C/2.16 kg | 29.0 | cm³/10min | |
| 265°C/5.0 kg | 75.0 | cm³/10min |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6180 | MPa | ASTM D638 |
| -- | 5890 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 99.0 | MPa | ASTM D638 |
| Yield | 95.0 | MPa | ISO 527-2/5 |
| Break 3 | 98.0 | MPa | ASTM D638 |
| Break | 103 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.7 | % | ASTM D638 |
| Yield | 2.1 | % | ISO 527-2/5 |
| Break 5 | 8.6 | % | ASTM D638 |
| Break 6 | 2.8 | % | ASTM D638 |
| Break | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 7 | 5580 | MPa | ASTM D790 |
| -- | 5480 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 148 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 148 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 148 | MPa | ASTM D790 |
| Flexural Strain at Break 10 | 3.4 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 11(23°C) | 24 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 58 | J/m | ASTM D256 |
| -30°C 12 | 4.0 | kJ/m² | ISO 180/1A |
| 23°C 13 | 4.1 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 220 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 173 | °C | |
| Vicat Softening Temperature | |||
| -- | 224 | °C | ASTM D1525 14 |
| -- | 222 | °C | ISO 306/A50, ISO 306/A120 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | 5.0 mm/min |
| 6 . | Type I, 5.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 2 mm/min |
| 11 . | 80*10*4 mm, Cut |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Wire & Cable GA-1057H1-VW1LF | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Wire & Cable |
| Sylvin 2930-67LG Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| DOMAMID® 6G60HCE | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| Huafon GW-100 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| LNP™ LUBRICOMP™ KFL36 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |