ELITE™ 5110G
| Category: | EPE , Enhanced Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ELITE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R99L54_ELITE-5110G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
ELITE™ 5110G Enhanced Polyethylene Resin is a copolymer produced via INSITE™ Technology from Dow Plastics. It offers a unique combination of high modulus and excellent impact strength, allowing for downgauging in bag applications. ELITE 5110 resin has excellent tensile strength and good tear properties. It complies U.S. FDA regulation 21 CFR 177.1520 (c) 3.2a when used unmodified and processed according to good manufacturing practices. Please contact your nearest Dow office regarding food contact compliance statements. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.926 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.85 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Film Puncture Energy (51 µm) | 6.91 | J | Internal method |
| Film Puncture Force (51 µm) | 97.0 | N | Internal method |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 51 µm | 277 | MPa | ASTM D882 |
| 2% secant, TD : 51 µm | 330 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 13.9 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 14.6 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 57.5 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 51.9 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 600 | % | ASTM D882 |
| TD : Fracture, 51 µm | 660 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | 410 | g | ASTM D1709B |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 560 | g | ASTM D1922 |
| TD : 51 µm | 1100 | g | ASTM D1922 |
| Seal Initiation Temperature 1(51 µm) | 120 | °C | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 111 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 123 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.8 µm) | 60 | ASTM D2457 | |
| Haze (50.8 µm) | 13 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 216 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：2.5 英寸 (63.5 mm)；24:1 L/D 螺杆类型：阻隔螺杆 模具间隙：70 密尔 (1.8 mm) 熔体温度：420°F (216°C) 输出：模具周长的 6 磅/小时/英寸 模具直径：6 英寸 放大比：2.5:1 螺杆速度：45 rpm 冷冻线高度：25 英寸 (635mm) |
| Note Message | |
|---|---|
| 1 . | Achieve a temperature of 2 psig (8.8 N/25.4mm) heat seal strength. J & B automatic heat sealing and thermal viscosity tester 0.5 S holding pressure, 40 psi pressure, Instron pulling speed 1.0 inches/min. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2305 A UV | RTP Company | TPU-Polyester | RTP |
| Ryton® PR11 | Solvay Specialty Polymers | PPS | Ryton® |
| UBE Nylon 1013 NW8 | UBE Engineering Plastics, S.A. | Nylon 6 | UBE Nylon |
| ASTALAC™ ASA 302 | Marplex Australia Pty. Ltd. | ASA | ASTALAC™ |
| MAJ'ECO DP374WR | AD majoris | PP, Unspecified | MAJ'ECO |