| PBT+PC, Unreinforced, impact modified thermoplastic alloy. Outstanding impact at low temperature |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Specific Volume | 0.838 | cm³/g | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 1.6 to 1.8 | % | |
| Across Flow : 3.20 mm | 1.6 to 1.8 | % | |
| Water Absorption (24 hr) | 0.080 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 108 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 43.4 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 180 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 1720 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 50.0 mm Span) | 64.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 670 | J/m | |
| 23°C | 900 | J/m | |
| Unnotched Izod Impact (23°C) | 1600 | J/m | ASTM D4812 |
| Gardner Impact | ASTM D3029 | ||
| 23°C 5 | 54.2 | J | |
| 23°C | 54.2 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 93.0 | °C | |
| 0.45 MPa, Unannealed, 6.40 mm | 98.9 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 53.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 60.0 | °C | |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 9.4E-5 | cm/cm/°C | |
| Flow : 60 to 138°C | 1.0E-4 | cm/cm/°C | |
| Transverse : -40 to 40°C | 9.8E-5 | cm/cm/°C | |
| RTI Elec | 75.0 | °C | UL 746 |
| RTI Imp | 75.0 | °C | UL 746 |
| RTI Str | 75.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 5.5E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| 1.60 mm, in Oil | 28 | kV/mm | |
| 3.20 mm, in Air | 19 | kV/mm | |
| 3.20 mm, in Oil | 19 | kV/mm | |
| Dielectric Constant | ASTM D150 | ||
| 100 Hz | 3.10 | ||
| 100 kHz | 3.00 | ||
| 1 MHz | 3.00 | ||
| Dissipation Factor | ASTM D150 | ||
| 100 Hz | 2.0E-3 | ||
| 100 kHz | 0.020 | ||
| 1 MHz | 0.020 | ||
| Arc Resistance 6 | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.47 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 116 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 50 to 80 | % | |
| Rear Temperature | 227 to 243 | °C | |
| Middle Temperature | 232 to 249 | °C | |
| Front Temperature | 238 to 260 | °C | |
| Nozzle Temperature | 238 to 260 | °C | |
| Processing (Melt) Temp | 238 to 260 | °C | |
| Mold Temperature | 48.9 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.345 | MPa | |
| Vent Depth | 0.013 to 0.020 | mm |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Modified |
| 6 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® A RV250K 100 NAT | Radici Plastics | Nylon 66 | Radilon® |
| Nymax™ 600 A HS Natural A | PolyOne Corporation | Nylon 6 Alloy | Nymax™ |
| Chemlon® 143 GH | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Flontech® FT-BRR30-8 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| HiFill® PC/PBT IM 6702 | Techmer Engineered Solutions | PC+PBT | HiFill® |