ASTAMID™ MB3L
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R8ypDL_ASTAMID-MB3L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTAMID™ MB3L is an Impact Modified, heat stabilised Polyamide 6 (PA 6 or Nylon 6). Note: The letters "U", "W" or "UV" indicate UV stabilisation has been added [ ie: ASTAMID™ MB3LU ]. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (235°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Water Absorption (equilibrium, 23°C, 50%) | 2.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(3.20 mm) | 2750 | MPa | ASTM D638 |
| Tensile Strength 2(3.20 mm) | 70.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 3.20 mm) | 5.0 | % | ASTM D638 |
| Flexural Modulus 4(3.20 mm) | 2350 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 170 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 150 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 65.0 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 250 - 255 | °C | |
| Middle Temperature | 255 - 265 | °C | |
| Front Temperature | 265 - 270 | °C | |
| Processing (Melt) Temp | 255 - 265 | °C | |
| Mold Temperature | 50.0 - 80.0 | °C | |
| Injection Pressure | 60.0 - 120 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.100 - 0.500 | MPa | |
| Screw Speed | 40 - 60 | rpm | |
| Clamp Tonnage | 3.0 - 5.0 | kN/cm² |
| Injection instructions |
|---|
| Drying Time (Opened Bag): >12 hr |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 805 CC UV | RTP Company | Acetal (POM) Copolymer | RTP |
| Moplen RP220M | LyondellBasell Industries | PP Random Copolymer | Moplen |
| Moplen PPU 1752HL23 | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| ASI POLYETHYLENE LP 390-01 | A. Schulman Inc. | HDPE Copolymer | ASI POLYETHYLENE |
| PAmpellonne® rgr_wss | Politem Plastik Ltd. | Nylon 66 | PAmpellonne® |