TECHNYL® A 20 V25 NATURAL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R8gPvF_TECHNYL-A-20-V25-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® A 20 V25 is a 25% glass fiber reinforced Red Phosphorous flame retarded grade based on a polyamide 66 resin. This product is heat stabiised for optimised injection moulding. This product is available in Natural & Black. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.38 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.90 | -- | % | |
| Flow | 0.50 | -- | % | |
| Water Absorption (23°C, 24 hr) | 0.75 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 0.550 | -- | Internal Method |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Fire and Smoke F Index | I3/F3 | -- | NF F16-101 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9000 | 6500 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 140 | 105 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 2.0 | 4.1 | % | ISO 527-2/1A |
| Flexural Modulus | 7500 | 6000 | MPa | ISO 178 |
| Flexural Stress | 250 | 155 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 50 | 60 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 8.0 | 9.0 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 250 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 263 | -- | °C | ISO 11357-3 |
| CLTE - Flow (23 to 85°C) | 3.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 25 | 25 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.40 | 4.00 | IEC 60250 | |
| Dissipation Factor | 0.020 | 0.050 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 400 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | V-0 | -- | ||
| 1.60 mm | V-0 | -- | ||
| 3.20 mm | V-0 | -- | ||
| Glow Wire Flammability Index (1.60 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.60 mm) | 725 | -- | °C | IEC 60695-2-13 |
| Oxygen Index | 31 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 270 to 275 | °C | |
| Middle Temperature | 275 to 280 | °C | |
| Front Temperature | 280 to 285 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU F595FCOO | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Tecnoflon® FOR 5312K | Solvay Specialty Polymers | Fluorelastomer | Tecnoflon® |
| Comai 664-3 BL | Comai Ltda | LLDPE | Comai |
| Guang Sung PVC GPMA95 | Guang Sung Plastics (GSPL) | PVC, Flexible | Guang Sung PVC |
| Sylvin 6234-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |