NEALID XG390
| Category: | Nylon+Olefin , Polyamide + Polyolefin |
| Manufacturer: | AD majoris |
| Trademark: | NEALID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R86GdO_NEALID-XG390.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NEALID XG390 is a glass fibre reinforced polyamide alloy intended for Injection moulding. APPLICATIONS NEALID XG390 has been developed especially for very demanding applications in automotive industry and electrical parts. Products requiring excellent combination between thermal and mechanical properties. NEALID XG390 is available in both natural (NEALID XG390) and black (NEALID XG390-8229) but other colours can be provided on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.33 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.30 to 0.70 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.90 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9200 | 8750 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 130 | 114 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 8050 | 7780 | MPa | ISO 178 |
| Flexural Stress | 190 | 175 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 15 | 17 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 43 | 47 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 245 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 228 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+15 | 1.0E+15 | ohms | DIN 53482 |
| Volume Resistivity | 1.0E+15 | 1.0E+15 | ohms·cm | DIN 53482 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 245 to 270 | °C | |
| Middle Temperature | 250 to 280 | °C | |
| Front Temperature | 245 to 270 | °C | |
| Nozzle Temperature | 245 to 275 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Pressure | 85.0 to 110 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2200 HF AR 20 | RTP Company | PEEK | RTP |
| megol® DP2268/65PA12 | API SpA | SEBS | megol® |
| Aegis® H120MP | Honeywell | Nylon 6 | Aegis® |
| EPO-TEK® 930-4 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| LUVOCOM® 1105/XCF/30 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |