Bapolene® PP5010
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Bamberger Polymers, Inc. |
| Trademark: | Bapolene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R7S5nA_Bapolene-PP5010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Bapolene PP5010 is an extrusion PP high impact copolymer with excellent color and processability. It offers extra high impact strength and low temperature properties. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 27.6 | MPa | ASTM D638 |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 15 | % | |
| Break | > 500 | % | |
| Flexural Modulus - 1% Secant (50.8 mm) | 1310 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 87.0 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Urochem 171 | Chemiplastica, Inc. | Urea Formald | Urochem |
| NYLEM® 6 GFR 20 | EMAS Plastik San.Tic.AS. | Nylon 6 | NYLEM® |
| Gallonprene® GP520-3009 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| HiPrene® HSG43BE | GS Caltex | PP, Unspecified | HiPrene® |
| Perlast® ICE G75LT | Precision Polymer Engineering Ltd. | Perfluoroelastomer | Perlast® |