MAJORIS PBT 9238 30 FV
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R7MyZQ_MAJORIS-PBT-9238-30-FV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PBT 9238 30 FV is a glass fiber reinforced polybutylene terephthalate, fireproofed UL94 V0 for injection molding. Raised oxygen index, excellent dimensional stability, great rigidity and a high thermal behavior allowing a peak use temperature at 200°C. APPLICATIONS PBT 9238 30 FV is used for injection applications in electrotechnical industry: for example circuit breaker, fuse holder, electronic components (connectors). This product is available in a large variety of different colors to be supplied on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.66 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction : 3.00mm | 0.70 | % | ISO 294-4 |
| Flow direction : 3.00mm | 0.50 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.020 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 215 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11300 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 9600 | MPa | ISO 178 |
| Flexural Stress | 220 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 210 | °C | ISO 75-2/A |
| Melting Temperature | 225 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (2.00 mm) | 23 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | IEC 60112 | ||
| Solution a | 250 | V | IEC 60112 |
| Solution B | 125 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 32 | % | ISO 4589-2 |
| Additional Information |
|---|
| Total Resistance of Insulation, NF C 26-210: 1e14 ohms |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 240 - 250 | °C | |
| Front Temperature | 250 - 260 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2200 AR 20 | RTP Company | PEEK | RTP |
| SCHULADUR® A3 GF 30 LM | A. Schulman Europe | PBT+ASA | SCHULADUR® |
| NYCOA Polyamide 1976 | Nycoa (Nylon Corporation of America) | Nylon 6 Alloy | NYCOA Polyamide |
| FLEXITEQ™ F75A113UV | Marplex Australia Pty. Ltd. | TPV | FLEXITEQ™ |
| ESTOPLAST XU 215BB10 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |