Ultramid® A3EG3
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R6hNNg_Ultramid-A3EG3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid A3EG3 is a 15% glass fiber reinforced injection molding PA66 grade. Applications Typical applications include medium stiffness machinery components and housings, as well as electrically insulating parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.24 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 70.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.18 mm) | 0.55 | -- | % | |
| Water Absorption | ||||
| Saturation | 7.0 | -- | % | ASTM D570 |
| Saturation, 23°C | 7.0 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 2.2 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.2 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 6000 | 4500 | MPa | ISO 527-2 |
| Tensile Strength | ||||
| Break, 23°C | 114 | -- | MPa | ASTM D638 |
| Break, -40°C | 156 | -- | MPa | ISO 527-2 |
| Break, 23°C | 130 | 85.0 | MPa | ISO 527-2 |
| Tensile Elongation | ||||
| Break, 23°C | 3.0 | -- | % | ASTM D638 |
| Break, 23°C | 3.0 | 10 | % | ISO 527-2 |
| Flexural Modulus | ||||
| 23°C | 5170 | -- | MPa | ASTM D790 |
| 23°C | 5200 | 4000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 180 | 125 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 7.0 | -- | kJ/m² | |
| 23°C | 8.0 | 11 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 43 | -- | kJ/m² | |
| 23°C | 45 | 70 | kJ/m² | |
| Notched Izod Impact | ||||
| -40°C | 53 | -- | J/m | ASTM D256 |
| 23°C | 59 | -- | J/m | ASTM D256 |
| 23°C | 5.5 | 14 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 250 | -- | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | -- | °C | ASTM D648, ISO 75-2/A |
| Peak Melting Temperature | 260 | -- | °C | ASTM D3418, ISO 3146 |
| CLTE | ||||
| Flow | 2.0E-5 | -- | cm/cm/°C | ASTM E831 |
| Flow | 3.3E-5 | -- | cm/cm/°C | |
| Transverse | 7.5E-5 | -- | cm/cm/°C | |
| RTI Elec | UL 746 | |||
| 0.800 mm | 130 | -- | °C | |
| 1.50 mm | 130 | -- | °C | |
| 3.00 mm | 130 | -- | °C | |
| RTI Imp | UL 746 | |||
| 1.50 mm | 125 | -- | °C | |
| 3.00 mm | 125 | -- | °C | |
| RTI Str | UL 746 | |||
| 1.50 mm | 125 | -- | °C | |
| 3.00 mm | 125 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | ||||
| 1.50 mm | 1.0E+13 | 1.0E+10 | ohms·cm | ASTM D257 |
| -- | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.50 | 5.50 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.014 | 0.30 | ||
| 1 MHz | 0.023 | 0.16 | ||
| Comparative Tracking Index | 550 | 550 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 280 to 305 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEETEC PP H7700 | LG Chem Ltd. | PP Homopolymer | SEETEC PP |
| TEREZ PC/ASA Blend 2002 | TER HELL PLASTIC GMBH | ASA+PC | TEREZ PC/ASA |
| EPO-TEK® 320 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Lupoy® GN1004FA | LG Chem Ltd. | PC | Lupoy® |
| LNP™ LUBRICOMP™ WFL34H compound | SABIC Innovative Plastics | PBT | LNP™ LUBRICOMP™ |