Edistir® ICE R 830D
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Edistir® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R6dHgS_Edistir-ICE-R-830D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Environmental stress cracking resistant (ESCR) HIPS. ICE R 830D combines high impact strength with an improved chemical resistance to oils, fats and chemical agents, such as detergents for both industrial and domestic use. Developed in particular for the fridge sector where hydrocarbons or freons are used as blowing agents for PU insulating foams. Designation: Thermoplastics ISO 2897-PS-I,G,O88-O3-O7-12 Applications This grade is suitable for extrusion/thermoforming and injection moulding. Typical applications are inner liners and frames for refrigerators and packaging containers for fatty foods. ICE R 830D significantly improves the wall thickness distribution in thermoforming and allows to optimize the thickness of the original extruded sheet. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Apparent Density | 0.65 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 - 0.70 | % | Internal method |
| Water Absorption (23°C, 24 hr) | < 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 51 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1450 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 16.0 | MPa | ISO 527-2/50 |
| Fracture | 23.5 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 70 | % | ISO 527-2/50 |
| Flexural Stress 1 | 35.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 130 | J/m | ISO 180/4A |
| -30°C | 8.0 | kJ/m² | ISO 180/1A |
| 23°C | 10 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 82.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 96.0 | °C | ISO 306/A50 |
| -- | 88.0 | °C | ISO 306/B50 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.17 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.5E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 7.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 65 | kV/mm | IEC 60243-1 |
| Dielectric Constant (50 Hz) | 2.50 | IEC 60250 | |
| Dissipation Factor (50 Hz) | 3.0E-4 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, All Colors) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 210 - 260 | °C | |
| Mold Temperature | 20.0 - 60.0 | °C |
| Injection instructions |
|---|
| Predrying normally not required |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 210 - 240 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4708 | RTP Company | PTT | RTP |
| ALTECH® PP-H A 4940/106 MR40 | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| Hifax TRC 432P G14008 | LyondellBasell Industries | PP Copolymer | Hifax |
| LUVOCOM® 1105-7720/BE | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| CABELEC® CA3896 | Cabot Corporation | PS (GPPS) | CABELEC® |