LEXAN™ ML9103R resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R6FGPs_LEXAN-ML9103R-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sheet extrusion grade |
| General Information | |
|---|---|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Water Absorption (24 hr) | 0.15 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 73.0 | MPa | Internal Method |
| Tensile Elongation (Break) | 270 | % | Internal Method |
| Flexural Modulus | 2200 | MPa | ASTM D790 |
| Flexural Strength | 89.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 820 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.20 mm) | 131 | °C | ASTM D648 |
| CLTE - Flow (-30 to 30°C) | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1776 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| TULAMID® PA-IR | UCC Shchekinoazot | Nylon 6 | TULAMID® |
| Xuchuan XCS-2067T | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| HiFill® ABS GF20 FR | Techmer Engineered Solutions | ABS | HiFill® |
| ALTECH® PA6 A 4230/140 MR20 GF10 FR | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |