SABIC® PP QR674K
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R5MEH8_SABIC-PP-QR674K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PP QR674K is a high melt flow index random copolymer with excellent transparency and good antistatic properties. This grade combines improved aesthetics of the finished articles with low temperature processability and a very good organoleptic performance. Part aesthetics are not affected by the lower temperatures, providing for a broader operating window. The SABIC®PP QR674K presents excellent flow behaviour, easy demoulding and good stiffness to impact ratio. SABIC® PP QR674K is mainly used in injection moulding processes. The SABIC® PP QR674K aims at transparent applications were higher MFI's with good flow are required. Its intended applications include injection moulded housewares, office & home storage boxes, thin wall packaging, lids and caps & closures. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 40 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 | ASTM D785 | |
| Shore Hardness (Shore D) | 64 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant 1 | 1200 | MPa | ASTM D638 |
| -- | 1150 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield 2 | 29.0 | MPa | ASTM D638 |
| Yield | 29.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 3 | 13 | % | ASTM D638 |
| Yield | 13 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0°C | 2.0 | kJ/m² | |
| 23°C | 4.5 | kJ/m² | |
| Notched Izod Impact | |||
| 0°C | 25 | J/m | ASTM D256A |
| 23°C | 45 | J/m | ASTM D256A |
| 0°C | 2.0 | kJ/m² | ISO 180/1A |
| 23°C | 4.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 80.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 4 | 75.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 57.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 52.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 125 | °C | ASTM D1525, ISO 306/A120 5 6 |
| -- | 70.0 | °C | ASTM D1525, ISO 306/B120 6 7 |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| 5 . | testbar 80*10*4mm |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ateva® 1850A | Celanese EVA Performance Polymers | EVA | Ateva® |
| EverGlide® MB5225 | Polymer Dynamix | PE, Unspecified | EverGlide® |
| DJSilicone NE-8171 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Ferro PP NPP00GD01BK | Ferro Corporation | PP, Unspecified | Ferro PP |
| GAPEX® HPP20GR56BK | Ferro Corporation | PP Homopolymer | GAPEX® |