Epocast 167 A/B
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Huntsman Advanced Materials |
| Trademark: | Epocast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R4wGAv_Epocast-167-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DESCRIPTION: Epocast® 167-A/B epoxy syntactic is a low-density, white, two-part system designed for insert potting and edge trim bonding in light weight honeycomb applications requiring a pourable, room-temperature curable material. Epocast® 167-A/B epoxy syntactic is qualified to BMS 5-28, Type 1. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D1622 | ||
| -- 1 | 0.600 | g/cm³ | ASTM D1622 |
| -- 2 | 0.700 | g/cm³ | ASTM D1622 |
| -- 3 | 1.00 | g/cm³ | ASTM D1622 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Modulus | 2070 | MPa | ASTM D695 |
| Compressive Strength (25°C) | 41.4 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 4 | 60.0 | °C |
| Flammability | Nominal Value | ||
|---|---|---|---|
| Flammability | Self-extinguishing |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time - 50 gms (25°C) | 0.8 - 1.2 | hr | ASTM D2471 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Lap Shear - chromic acid etched aluminum (25°C) | 10.3 | MPa | ASTM D1002 |
| Weight Gain 5 | ASTM D543 | ||
| Distilled water : 25°C | 1.0 | % | ASTM D543 |
| Mil-M-5606, hydraulic fluid : 25°C | 1.5 | % | ASTM D543 |
| Skydrol 500-A : 25°C | 3.5 | % | ASTM D543 |
| TT-S-735, Type III test fluid : 25°C | 1.0 | % | ASTM D543 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Resin | Mixing ratio by weight: 100 | ||
| Hardening method | Mixing ratio by weight: 15 | ||
| Thermoset Mix Viscosity | ASTM D2196 | ||
| 25°C 6 | 20000 | cP | ASTM D2196 |
| 25°C 7 | 45000 | cP | ASTM D2196 |
| 25°C 8 | 800 | cP | ASTM D2196 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CURE SCHEDULE: 24 hours at 77°F (25°C) or gel at room temperature plus 5 hours at 125°F (52°C). |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | System |
| 3 . | Hardener |
| 4 . | TMA |
| 5 . | on immersion - 24 hrs |
| 6 . | System |
| 7 . | Resin |
| 8 . | Hardener |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD A 102 | RTP Company | PP Copolymer | RTP |
| Trademark PP PPH1200MA | Trademark Plastics Corporation | PP Homopolymer | Trademark PP |
| NEXT REGRIND POMC M90-300RG | NEXT Specialty Resins, Inc. | Acetal (POM) Copolymer | NEXT REGRIND |
| Badamid® PA12 GF30 TM-Z1 FR HF natur S4 | Bada AG | Nylon 12 | Badamid® |
| LNP™ LUBRICOMP™ QFL36 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ LUBRICOMP™ |