Trexprene® A75SCI-HF
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Mitsubishi Chemical Performance Polymers, Inc. |
| Trademark: | Trexprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R4qz5p_Trexprene-A75SCI-HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Product Description: TREXPRENE ® A75SCI-HF is a heat stabilized PP/EPDM based Thermoplastic Vulcanized Elastomer (TPV) which contains a lubricant/slip package for lower co-efficient of friction and anti-wear properties versus normal TPV's. This compound is formulated in pre-color form primarily for underhood or interior applications. This material can be processed using Injection Molding, Extrusion, Blow Molding or other melt processing techniques. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.880 to 0.940 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 15 sec) | 74 to 82 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Wear Resistance 1 | No appreciable loss of grain, texture or color | ASTM D3844 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fogging - Dry Fog | 79 | % | SAE J1756 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Color Fastness - to Light 2 | Delta E < 3 | ||
| Linting 3 | Rating less than 2 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress - Across Flow 4(100% Strain) | 3.20 | MPa | ISO 37 |
| Tensile Stress - Across Flow 5(Break) | 7.00 | MPa | ISO 37 |
| Tensile Elongation - Across Flow 6(Break) | 690 | % | ISO 37 |
| Tear Strength - Across Flow 7 | 41 | kN/m | ISO 34-1 |
| Compression Set | |||
| 23°C, 22 hr | < 37 | % | ASTM D395B |
| 100°C, 70 hr | < 49 | % | ASTM D395B |
| 23°C, 22 hr 8 | < 37 | % | ISO 815 |
| 100°C, 70 hr 9 | < 49 | % | ISO 815 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | |||
| -- | < -54.0 | °C | ASTM D746 |
| Type B | < -54.0 | °C | ISO 812 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 19 | mm/min | ISO 3795 |
| Note Message | |
|---|---|
| 1 . | 1000 cycles CS10 Wheel (500 g load) |
| 2 . | SAE J2412, ISO 105-B06, Cond. 5, 1,240.8 kJ/m² |
| 3 . | LP-463KB-37-01, Method A |
| 4 . | Type 1, 500 mm/min |
| 5 . | Type 1, 500 mm/min |
| 6 . | Type 1, 500 mm/min |
| 7 . | Method Ba, Angle (Unnicked), 500 mm/min |
| 8 . | Type A |
| 9 . | Type A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren M3500CA (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| AKROMID® B3 GF 30 1 L black (4491) | AKRO-PLASTIC GmbH | Nylon 6+PP | AKROMID® |
| Latishield 66-10A G/15 | LATI S.p.A. | Nylon 66 | Latishield |
| POLYfill PPHC T15020 | Polykemi AB | PP, Unspecified | POLYfill |
| Hifax X M1 T11 BLACK | LyondellBasell Industries | PP Copolymer | Hifax |