SABIC® HDPE PCG4906
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R3IwhX_SABIC-HDPE-PCG4906.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® HDPE PCG4906 is typically used for the blow moulding of healthcare industrial packaging (IBC, open head and tight head drums, jerry cans). The product features good stiffness/ESCR balance combined with good process ability. Compliance to regulations. SABIC® HDPE PCG4906 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.949 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 6.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 950 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00 mm, Compression Molded | 23.0 | MPa | |
| Break, 2.00 mm, Compression Molded | 34.0 | MPa | |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | > 1000 | % | ISO 527-2/1BA/50 |
| Flexural Modulus (2.00 mm, Compression Molded) | 1000 | MPa | ISO 178 |
| Flexural Stress (2.00 mm, Compression Molded) | 24.0 | MPa | ISO 178 |
| ESCR (Strain Hardening) - Gp | 30.0 | MPa | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Enthalpy Change | 192 | J/g | ISO 11357-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (-30°C, Compression Molded) | 17 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 77.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 126 | °C | ISO 306/A |
| Melting Temperature (DSC) | 131 | °C | ISO 11357-3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXUS PC/ABS PC/ABSQX7004 | Nexus Resin Group, LLC. | PC+ABS | NEXUS PC/ABS |
| Akulon® K225-KV | DSM Engineering Plastics | Nylon 6 | Akulon® |
| Celanex® 3309HRLM | Celanese Corporation | PBT | Celanex® |
| ASTALON™ K2000G2 | Marplex Australia Pty. Ltd. | PC | ASTALON™ |
| Karina WHITE PVC COMPOUND 10/1-FC (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |