LNP™ LUBRICOMP™ DBL349E compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R1whbF_LNP-LUBRICOMP-DBL349E-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* DBL349E is a compound based on Polycarbonate resin containing 20% Glass Bead, 15% PTFE. Added features of this material include: Wear Resistant, Flame Retardant. Also known as: LNP* LUBRICOMP* Compound DBL-4034 EM FR Product reorder name: DBL349E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.40 to 0.60 | % | ASTM D955 |
| Across Flow : 24 hr | 0.60 to 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 0.69 | % | ISO 294-4 |
| Flow : 24 hr | 0.54 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3450 | MPa | ASTM D638 |
| -- | 2970 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 41.4 | MPa | ASTM D638 |
| Yield | 41.0 | MPa | ISO 527-2 |
| Break | 37.9 | MPa | ASTM D638 |
| Break | 38.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.9 | % | ASTM D638, ISO 527-2 |
| Break | 9.0 | % | ASTM D638 |
| Break | 7.6 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2760 | MPa | ASTM D790 |
| -- | 2900 | MPa | ISO 178 |
| Flexural Stress | 78.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.52 | ||
| vs. Itself - Static | 0.70 | ||
| Wear Factor - Washer | 90.5 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 2 | 5.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 460 | J/m | ASTM D4812 |
| 23°C 3 | 31 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 15.7 | J | ASTM D3763 |
| -- | 4.50 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 141 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 140 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 129 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 129 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 6.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Transverse : -40 to 40°C | 6.5E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 6.4E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DOWLEX™ 2085G | The Dow Chemical Company | LLDPE | DOWLEX™ |
| Hanwha Total PP GB33R | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Jackdaw ABS/PC FX70BK6583 | Jackdaw Polymers | PC+ABS | Jackdaw ABS/PC |
| Karina GRAY PVC COMPOUND 701-18/473-F-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ STAT-KON™ DD0009 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |