Epiall® 1908-1
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Sumitomo Bakelite North America, Inc. |
| Trademark: | Epiall® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R1tCFq_Epiall-1908-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Epiall 1908-1 is a short fiberglass reinforced epoxy molding compound, with excellent dimensional stability, good strength properties and good electrical insulation properties that meets the requirements of ASTM D5948 Type GEI-5. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.92 | g/cm³ | ASTM D792 |
| Apparent Density | 0.90 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow (Compression Molded) | 0.20 to 0.40 | % | ASTM D955 |
| Water Absorption - 48 hr (50°C) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 80.0 | MPa | ASTM D638 |
| Flexural Modulus (Compression Molded) | 15100 | MPa | ASTM D790 |
| Flexural Strength (Break) | 130 | MPa | ASTM D790 |
| Compressive Strength | 240 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 37 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed, Compression Molded) | > 282 | °C | ASTM D648 |
| CLTE - Flow | 3.7E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.73 | W/m/K | ASTM C177 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI Str | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | ASTM D149 | ||
| -- 2 | 14 | kV/mm | |
| -- 3 | 13 | kV/mm | |
| Dielectric Constant 4(1 MHz) | 4.10 | ASTM D2520 | |
| Dissipation Factor 5(1 MHz) | 0.020 | ASTM D150 | |
| Arc Resistance | 180 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (6.40 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | Wet, 60 Hz |
| 2 . | Method A (Short-Time) |
| 3 . | Method B (Step-by-Step) |
| 4 . | Wet |
| 5 . | Wet |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ PD 2201 | PolyOne Corporation | PP, Unspecified | Maxxam™ |
| Boltaron 9200 | Boltaron Performance Products | PMMA+PVC | Boltaron |
| Lifoflex® UV 90 GA 1090 | ELASTO | SEBS | Lifoflex® |
| Petrothene® LB560200 | LyondellBasell Industries | HDPE | Petrothene® |
| ALCOM® PP 620/40 IM UV VT1022-13MCX | ALBIS PLASTIC GmbH | PP, Unspecified | ALCOM® PP |