SABIC® PP 531P
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R1L86v_SABIC-PP-531P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PP 531P has a high molecular weight and therefore mainly used for extrusion. It can be used for non-pressure pipes and sheet applications. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.30 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 107 | ASTM D785 | |
| Shore Hardness (Shore D) | 70 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant 1 | 1600 | MPa | ASTM D638 |
| -- | 1600 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield 2 | 38.0 | MPa | ASTM D638 |
| Yield | 37.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 3 | 8.0 | % | ASTM D638 |
| Yield | 9.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 2.5 | kJ/m² | |
| 0°C | 3.5 | kJ/m² | |
| 23°C | 6.0 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| -20°C | 25 | J/m | ASTM D256A |
| 0°C | 35 | J/m | ASTM D256A |
| 23°C | 60 | J/m | ASTM D256A |
| -20°C | 2.5 | kJ/m² | ISO 180/1A |
| 0°C | 3.5 | kJ/m² | ISO 180/1A |
| 23°C | 6.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 90.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 4 | 85.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 60.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 55.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 156 | °C | ASTM D1525, ISO 306/A120 5 6 |
| -- | 98.0 | °C | ASTM D1525, ISO 306/B120 6 7 |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| 5 . | testbar 80*10*4mm |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RELENE® D16501 | Reliance Industries Limited | HDPE | RELENE® |
| SCANAMID 66 A11^ X30 | Polykemi AB | Nylon 66 | SCANAMID 66 |
| Nypol® PA A3 T20 PRTA011 NR389 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| BCC Resins BC 9020 | BCC Products Inc. | Silicone | BCC Resins |
| Grilamid® XE 4108 black 9992 | EMS-GRIVORY | Nylon 6/12 | Grilamid® |