Akulon® F249-HG4
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Akulon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | R0ZY7F_Akulon-F249-HG4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Akulon® F249-HG4 is a Polyamide 6 (Nylon 6) material filled with 20% glass fiber. It is available in Europe for extrusion blow molding. Primary attribute of Akulon® F249-HG4: Heat Stabilizer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 8.0 | % | |
| Equilibrium, 23°C, 50% RH | 2.4 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.5 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 8.0 | kJ/m² | |
| 23°C | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 70 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 215 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 195 | °C | ISO 75-2/A |
| Melting Temperature 1 | 220 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 255 to 265 | °C | |
| Middle Temperature | 265 to 275 | °C | |
| Front Temperature | 265 to 280 | °C | |
| Nozzle Temperature | 260 to 280 | °C | |
| Processing (Melt) Temp | 250 to 285 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Versaflex™ CL2242 | PolyOne Corporation | TPE | Versaflex™ |
| Centrex® 810 | Network Polymers, Inc. | ASA | Centrex® |
| DJSilicone NE-G170 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Electroblend® PBT-1801 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PBT | Electroblend® |
| POCAN® KU 2-7503/1 000000 | LANXESS GmbH | PBT | POCAN® |