SCANBLEND FS7 FR UV
| Category: | ASA+PC , Acrylonitrile Styrene Acrylate + PC |
| Manufacturer: | Polykemi AB |
| Trademark: | SCANBLEND |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QznVGX_SCANBLEND-FS7-FR-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC/ASA Flame retardant / UV-stabilized |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 35 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.50 to 0.70 | % | |
| Flow | 0.50 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 45.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2400 | MPa | ISO 178 |
| Flexural Stress | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 35 | kJ/m² | |
| 23°C | 40 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, Unannealed | 120 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 100 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 135 | °C | ISO 306/A50 |
| -- | 120 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 960 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLON IR 1900 | POLYMA Kunststoff GmbH & Co. KG | PC | POLYLON |
| KRATON® RP6936 | Kraton Polymers LLC | SEBS | KRATON® |
| ISPLEN® RC 580 S2M | REPSOL | PP, Unspecified | ISPLEN® |
| Braskem PP DR7051.01 | Braskem Europe GmbH | PP Random Copolymer | Braskem PP |
| LNP™ STAT-KON™ WS002I compound | SABIC Innovative Plastics | PBT | LNP™ STAT-KON™ |