FLEXITEQ™ F50D000
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | FLEXITEQ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Qz4xwZ_FLEXITEQ-F50D000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FLEXITEQ™ F50D000 is a formulation based on Santoprene™ rubber technology, incorporating good strength, tear resistance and toughness. This material can be processed on conventional thermoplastic equipment for extrusion. It is polyolefin based and is completely recyclable. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw D | 60 | ASTM D2240 | |
| Shaw D, 15 seconds | 50 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus 1(3.20 mm) | 400 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | ASTM D412 | ||
| Yield | 16.0 | MPa | ASTM D412 |
| Fracture | 19.0 | MPa | ASTM D412 |
| Tensile Elongation 3(Break) | 600 | % | ASTM D412 |
| Tear Strength 4(23°C) | 110 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 520 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 130 | °C | ASTM D1525 5 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Cylinder Zone 1 Temp. | 185 - 205 | °C | |
| Cylinder Zone 3 Temp. | 195 - 220 | °C | |
| Cylinder Zone 5 Temp. | 200 - 230 | °C | |
| Melt Temperature | 200 - 230 | °C | |
| Die Temperature | 200 - 230 | °C | |
| Back Pressure | 5.00 - 20.0 | MPa |
| Extrusion instructions |
|---|
| Typical Mesh Screen Combination: 20/40/60 |
| Note Message | |
|---|---|
| 1 . | 1.3 mm/min |
| 2 . | C mold, 500 mm/min |
| 3 . | Mouth die C, 500 mm/min |
| 4 . | C mold, 500 mm/min |
| 5 . | 标准 B (120°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 802 TFE 15 | RTP Company | Acetal (POM) Copolymer | RTP |
| VINIKA® CE55EG | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| GAPEX® RPP30EB80HB NATURAL | Ferro Corporation | PP Homopolymer | GAPEX® |
| EPLAMID 6 GFR 50 NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 6 | EPLAMID 6 |
| LUVOCOM® 80-8511 | LEHVOSS Group | Acetal (POM) Copolymer | LUVOCOM® |