INEOS LDPE 28H430

Category:	LDPE , Low Density Polyethylene
Manufacturer:	INEOS Olefins & Polymers Europe
Trademark:	INEOS LDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Qynctm_INEOS-LDPE-28H430.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Applications

28H430 is particularly suitable for nappy film and other hygienic films made by cast film coextrusion or blending. It can also be processed in blown film for thin rigid films with good optical properties

Characteristics
28H430 is an autoclave LDPE homopolymer. It offers the following properties:

High rigidity

Good downgauging potential

Low blocking

MFR tailored for cast extrusion

Good drawdown

If corona treatment is necessary, the level should normally be in the range 38-48 mN/m.

General Information
Features	Rigidity, high Homopolymer Good stripping No additive
Uses	Films Mixing cast film
RoHS Compliance	Contact manufacturer
Forms	Particle
Processing Method	Blow film Co-extrusion molding Extrusion cast film

Physical	Nominal Value	Unit	Test Method
Density	0.930	g/cm³	ISO 1183/D
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	2.1	g/10 min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Coefficient of Friction	> 0.50		ASTM D1894

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	50	µm
Tensile Modulus			ISO 1184
1% secant, MD : 50 µm	290	MPa	ISO 1184
1% secant, TD : 50 µm	290	MPa	ISO 1184
Tensile Stress			ISO 1184
MD : Yield, 50 µm	14.0	MPa	ISO 1184
TD : Yield, 50 µm	16.0	MPa	ISO 1184
MD : Break, 50 µm	26.0	MPa	ISO 1184
TD : Break, 50 µm	22.0	MPa	ISO 1184
Tensile Elongation			ISO 1184
MD : Break, 50 µm	460	%	ISO 1184
TD : Break, 50 µm	660	%	ISO 1184
Dart Drop Impact (50 µm)	110	g	ASTM D1709A

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	97.0	°C	ISO 306/A50

Optical	Nominal Value	Unit	Test Method
Gloss (45°, 50.0 µm)	64		ASTM D2457
Haze (50.0 µm)	9.0	%	ASTM D1003

Extrusion	Nominal Value	Unit
Melt Temperature	240 - 280	°C

Extrusion instructions
Blown Film melt temperature range: 160 to 185°C

Resin Grade	Manufacturer	Category	Trademark
Spartech Polycom X05023	Spartech Polycom	PP Copolymer	Spartech
TAROMID A 280 R3	Taro Plast S.p.A.	Nylon 66	TAROMID A
Gallonprene® GP520-6001	Shenzhen Sungallon Rubber & Plastic Corporation Limited	TPE	Gallonprene®
Hylon® N2033STHL	Ravago Manufacturing Americas, LLC	Nylon 6	Hylon®
Sylvin 83025-80UV Natural	Sylvin Technologies Incorporated	PVC, Flexible	Sylvin