UBE Nylon 5034 C2
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | UBE Engineering Plastics, S.A. |
| Trademark: | UBE Nylon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QvnKsm_UBE-Nylon-5034-C2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UBE NYLON 5034 C2 is a high viscosity, nanocomposite Polyamide 6/6.6 copolymer, offering excellent barrier properties. The material is suitable for cast and air-cooled blown film production. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| With self-dynamics | 0.30 | ASTM D1894 | |
| With Self-Static | 0.30 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus - MD (Cast Film) | 750 | MPa | ASTM D882 |
| Tensile Strength - MD | ASTM D882 | ||
| Yield, extruded film | 30.0 | MPa | ASTM D882 |
| Fracture, extruded film | 105 | MPa | ASTM D882 |
| Tensile Elongation - MD (Fracture, Extruded Film) | 550 | % | ASTM D882 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 196 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss | 135 | ASTM D523 | |
| Haze | 3.0 | % | ASTM D1003 |
| Additional Information |
|---|
| The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.The value listed as Surface Resistivity, ASTM D257, was tested in accordance with UBE test methods.Oxygen Permeability, ASTM D3985: 25 ml/m²/dayRelative Viscosity, JIS K6810, 96% H2SO4, conc. 1.0 g/100 ml: 3.36Extractable Content, JIS K6810: <1.0 wt%Water Vapor Permeability, JIS Z0208: 80 g/m²/dayPiercing Strength, JAS P1019, Cast Film: 9.5 NPiercing Elongation, JAS P1019, Cast Film: 12 mmFlex Crack Resistance, MIL B131B, 23°C, 1000 cycle, Cast Film: <10 hole/0.04 m²Gelbo Test, MIL B131B, 5°C, 100 cycle, Cast Film: <10 hole/0.04 m² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Gallonprene® GP520-4004 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Sylvin 8354-62D Yellow 4193 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| SQUARE® LIM1939-56AE/BE | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |
| CALIBRE™ MEGARAD™ 2080-15 | Trinseo | PC | CALIBRE™ MEGARAD™ |
| EPAMOULD 665D12G30 | Epaflex Polyurethanes S.R.L. | TPU, Unspecified | EPAMOULD |